Abstract:The C=C double bonds in the main chain of hydroxyl-terminated polybutadiene (DHTPB), obtained by the degradation of polybutadiene rubber, were partially epoxided using m-chloroperoxybenzoic acid (mCPBA) as epoxidation reagent. A series of epoxided HTPBs (EHTPB) with different epoxy contents (5%, 10% and 15%) were prepared by tuning the molar ratio of mCPBA to C=C double bonds. The structures of EHTPBs were characterized by Fourier transform-infrared (FTIR), nuclear magnetic resonance (H-1-NMR) spectroscopy and gel permeation chromatography (GPC). The epoxy percent in EHTPBs from H-1-NMR spectra was in accordance with the design. In addition, a series of EHTPB-based polyurethane elastomers (EPU) were prepared by the reaction between EHTPB and 4,4'-diphenylmethane diisocyanate with 1,4-butanediol as a chain extender. Mechanical and thermal properties of the EPU samples were characterized by tensile test, differential scanning calorimetry (DSC) and thermal gravity analysis (TGA). With increased epoxy percent in EHTPB, the Young's modulus and the tensile strength of the EPU samples increased, whereas the elongation at break decreased. The sample EPU10 prepared with 10% of epoxy had the best mechanical properties with 8.82 MPa as Young's modulus, 7.83 MPa as tensile strength, and (485 +/- 23)% as elongation at break. The elasticity recovery of the EPU sample was slightly better than HTPB-based PU (EPU0). The results with TGA test showed that the thermal degradation of EPU, similar to EPU0, was divided into three stages. However, the EPU samples had better thermal stability with the initial degradation temperature at 210 degrees C, about 30 degrees C higher than that of EPU0. The DSC results showed that the glass transition temperature (T-g) of EPU gradually increased as epoxy percent was increased, though still lower than that of HTPB (FHTPB) based PUs prepared by free-radical polymerization.

Research of Epoxy Resin Insulation Coating Toughening Modified with Epoxidized Hydroxyl Terminated Polybutadiene

Preparation and Properties of Epoxided Hydroxyl-terminated Polybutadiene Based Polyurethane Elastomers

Modification of Unsaturated Polyester Resin by HTPB: Effect of Introducing Method of the Rubber

STUDY ON DGE-BHBTMBP/E-51/DDS CURED

Study on High Insulation and Low Dielectric Constant Type CTPB Modified Epoxy Resin

Study of Epoxy Resin Modified by Hydroxyl Terminated Polybutadiene

Toughening of bisphenol A and carboxyl-terminated butadiene-acrylonitrile to epoxy resin

MODICATION OF BISPHENOL A DICYANATE ESTER BY EPOXIDIZED HYDROXYL-TERMINATED POLYBUTADIENE

Isocyanate-terminated Polyethers Toughened Epoxy Resin:Chemical Modification,Thermal Properties,and Mechanical Strength

Study on the Dielectric Properties of the Epoxy Resin Toughened with Different Molecular Weight HTBN

Mechanical and dielectric properties of epoxy resin modified using reactive liquid rubber (HTPB)

Improving Elongation of Epoxy Outside Protective Coating

Modification of Epoxy Resin by Polyurethane Based on Polyether

Enhanced Mechanical and Dielectric Properties of an Epoxy Resin Modified with Hydroxyl-Terminated Polybutadiene

Thermal, mechanical, and dielectric properties of epoxy resin modified using carboxyl-terminated polybutadiene liquid rubber

Mechanical Properties of Modified Hydroxyl-Terminated Polybutadiene Based Polyurethane

Mixed Hyperbranched Poly(aryl Ether Ketone) Results in High Toughness and Excellent Thermal Resistance in Epoxy Resin

A Carboxyl-Terminated Polybutadiene Liquid Rubber Modified Epoxy Resin with Enhanced Toughness and Excellent Electrical Properties

Study on the Hyperbranched Polymer Modified Epoxy Resin

Dielectric properties of hydroxyl-terminated butadiene nitrile liquid rubber toughened Epoxy Resin polymer

Cyanate Ester Resin Modified by Hydroxyl‐terminated Polybutadiene: Morphology, Thermal, and Mechanical Properties