Isocyanate-terminated Polyethers Toughened Epoxy Resin:Chemical Modification,Thermal Properties,and Mechanical Strength

Cai Haopeng,Wang Jun,Wang Xiang,Xu Renxin

DOI: https://doi.org/10.1007/s11595-006-2256-6

2007-01-01

Abstract:The toughening of the diglycidyl ether of bisphenol A epoxy resin with isocyanate-terminated polyethers(ITPE)was investigated.The progress of the reaction and the structural changes during modification process were studied using FTIR spectroscopy.The studies support the proposition that TDI(tolylene diisocyanate)acts as a coupling agent between the epoxy and polyethers,forming a urethane linkage with the former and the latter,respectively.Me THPA-cured ER/ITPs blends were characterized using dynamic mechanical analysis(DMA)and thermogravimetric analysis(TGA).It is indicated the glass transition temperature(T g )of systems was lower than the T g of pure epoxy resin and overfull ITPE separated from the modified epoxy resin and formed another phase at an ITPE-content of more than 10wt%.The thermal stability was decreased by the introduction of ITPE.The impact strength and the flexural strength of the cured modified-epoxy increased with increasing the ITPE content and a maximum plateau value of about 24.03 kJ/m2 and 130.56 MPa was measured in 10wt%ITPE.From scanning electron microscopy(SEM)studies of the fractrue surfaces of ER/ITPE systems,the nature of the micromechanisms responsible for the increases in toughness of the systems was identified.