Reactivity Ratios and Copolymer Composition of Vinyl Chloride and N-Substituted Maleimide Copolymerization
M Du,ZX Weng,GR Shan,ZM Huang,ZR Pan
DOI: https://doi.org/10.3321/j.issn:0251-0790.2004.10.034
2004-01-01
Abstract:Radical copolymerization of vinyl chloride (VC) with N-substituted maleimide were conducted in tetrahydrofuran at 60 degreesC with AIBN as initiator. Based on the copolymer composition and monomer composition, the copolymerization parameters (r(1), r(2), Q and e) of each monomer pair were determined. The reactivity ratios of N-substituted maleimide monomers were all larger than that of VC, indicating that these monomers were more active. The effects of substituted groups on reactivity ratios were also discussed, and N-substituted maleimide monomer had a larger Q value than that of VC, especially for phenyl substituted maleimide monomer. It was believed that this phenomenon was related to the conjugated effect of phenyl group in N-substituted maleimide. The location of substituent on phenyl would influence Q value of N-substituted phenyl maleimide monomer. para-Substituent (i. e. p-CIPMI and p-MPMI) phenyl maleimide has a large Q value than that of ortho- and meta-substituted phenyl maleimides. In addition, there is a larger difference between e(1) and e(2), which means the large alternating tendency of the copolymerization of N-substituted maleimide with VC. The copolymer composition., for VC/N-substituted maleimide solution copolymerization varied greatly with conversion, especially for small N-substituted maleimide feed ratios. Subsequently, recurrence method deduced from Mayo-Lewis was used for predicting the change of copolymer composition with conversion. In addition, this method is also used to calculate the critical weight [(x(w))(c)] conversion for VC/N-substituted maleimide copolymerization systems at different VC monomer feed fractions.