Branching Copolymerization Of Styrene And Methyl Methacrylate With Divinylbenzene
Wenyan Huang,Dan Li,Bibiao Jiang,Dongliang Zhang,Yang Yang,Jianhai Chen,Guangqun Zhai,Lizhi Kong,Chunlin Liu,Fanghong Gong,Aiqing Lu
IF: 2.485
2010-01-01
Iranian Polymer Journal
Abstract:The branching copolymerization of styrene (St) and methyl methacrylate (MMA) with divinylbenzene (DVB) as branching agent was conducted using atom transfer radical polymerization (ATRP). The kinetics and extent of branching with respect to monomer conversion were studied in details. Gas chromatography (GC), proton nuclear magnetic resonance (H-1 NMR) spectroscopy and dual detection size exclusion chromatography (DD-SEC) were used to monitor the reactions and analyze the resulting copolymers. The analysis of reactants conversion revealed that the conversion rate of DVB, having two double bonds, is only slightly faster than those of the monomers, with no donor/acceptor interactions between DVB molecules and the monomers. The molecular weight increases slowly which is still somehow larger than the theoretical value in the early stages; then deviates significantly from the its theoretical estimation beyond 40% conversion and increases steeply at later stages of 70% monomer conversion. These results suggest that branching takes place in the early stages of the reaction regardless of any possible donor/acceptor interactions between the monomers and DVB molecules, and the coupling reaction originates mainly from the primary chain resulting in small chain branching. Coupling reaction between the branched chains becomes significant in the later stages of the copolymerization which produces highly branched chains. The reaction system contains three components throughout the reaction: the primary chains, the slightly branched chains comprising of two primary chains, and the highly branched chains consisting of 3 or more primary chains. Although the weight fraction of the branched chains increases with monomer conversion, there is finally 20% primary chains still left in the reaction system which gives rise to limited molecular weight and high polydispersity of the branched polymers prepared through ATRP using divinyl monomer as the branching agent.