Effects of Agitation Speed on the Average Diameter of PVC Suspension Resin
占晓强,尹建平,魏家福,安丰颖,黄富铭,刘中海,包永忠,黄志明
DOI: https://doi.org/10.3321/j.issn:1003-9015.2009.06.010
2009-01-01
Abstract:The law of polymerized PVC particle size varying with the conversion rate of vinyl chloride suspension polymerization was studied in a 5 L autoclave by respectively using two different agitation schemes, such as agitation with constant-speed and agitation with variable-speed. The results show that the above law for using these two agitation schemes are similar, i.e. when the conversion rate is low, the polymerized particle size increases gradually with the increase of conversion rate, while when the conversion rate reaches 15%, then the diameter of the polymerized particles will no longer change with the further increase of the conversion rate. Moreover, the polymerization parameters, such as the agitation speed, the dispersant amount used and the polymerization temperature only affect the final obtained PVC grain diameter and have little effect on the variation law of the obtained particle diameter with the conversion rate. In our study, the variable agitation scheme was adopted for the PVC suspension polymerization in a large-scale autoclave, and the effects of the time after which the agitation speed is changed, the former agitation speed and the later agitation speed on the polymerized PVC grain diameter and its distribution were studied. After calculating respectively the energy consumptions of the PVC suspension polymerization with above two agitation schemes, it was found that scheme of agitation with variable-speed not only benefits the formation of grains, but can also reduce the agitation power and save the energy consumption.