N-TERT-BUTYL-α-PHENYLNITRONE MEDIATED SUSPENSION POLYMERIZATION OF VINYL CHLORIDE

Ren-he Qiu,Guo-rong Shan

DOI: https://doi.org/10.3724/sp.j.1105.2012.11409

2012-01-01

Acta Polymerica Sinica

Abstract:The suspension polymerization of vinyl chloride (VC) was carried out at 40 similar to 70 degrees C in the composite dispersant system composed of poly(vinyl alcohol) and hydroxypropyl methylcellulose, with N-tert-butyl-alpha-phenylnitrone (PBN) as the source of nitroxide radicals and a-cumyl peroxyneodecanoate (Lup188) as initiator. The effects of the concentration of Lup188, the concentration of PBN and polymerization temperature on the polymerization kinetics, molecular weight and polydispersity index (PDI) of poly (vinyl chloride) (PVC) were investigated in detail. The kinetics of VC suspension polymerization was monitored by gravimetric method while the molecular weight and its distribution of PVC synthesized were determined by gel permeation chromatography. The results showed that the chain propagation in VC polymerization could be efficiently controlled by adding suitable amount of PBN and Lup188 at a reasonable temperature. The optimal molar ratio of VC, Lup188 and PBN was 1000:7:1. As the polymerization temperature increased, the polymerization rate of VC first increased and then decreased, which was different from the mechanism of common radical polymerization. Simultaneously, the molecular weight of synthesized PVC first increased and then decreased, while the PDI first decreased and then increased. The optimal polymerization temperature was 50 degrees C. At this temperature, the PDI of PVC was 1. 7 similar to 2.0 and did not change significantly in the range of conversion 3% similar to 50%, which was considerably lower than that in common radical polymerization. However, with the conversion increasing further, the PDI of PVC increased.