Kinetics and Particle Formation Mechanism of a New Vinyl Chloride Heterogeneous Polymerization

B.W.Brooks

DOI: https://doi.org/10.3321/j.issn:1003-9015.2002.06.008

2002-01-01

Abstract:The kinetics and particle formation mechanism of vinyl chloride (VC) heterogeneous polymerization using n-butane (But) as the reaction medium were studied. VC conversions were calculated from the vapor pressure or composition based on the vapor-liquid equilibrium equations of VC-But system. The polymerization induction period was not obvious and the self-acceleration phenomenon was occurred in the early and mid stages of the polymerization process. The volume average particle size of resulting poly(vinyl chloride) (PVC) resins produced by the proposed heterogeneous polymerization were close to that of conventional suspension PVC, while the number average particle size was much smaller. The PVC particles were constructed by primary particles, which were almost not fused together. The particle size of primary particles and porosity in the center of PVC particles were greater than that in the top layer of the particles. The cold plasticizer absorption of obtained PVC resin was much higher than that of conventional suspension PVC. The particle formation mechanism was proposed as following: PVC chains precipitate from the reaction medium to form domains, primary particles and particles in the early stage of polymerization. The increment of primary particles and their aggregation to the top layer of particle, growth of particles by capturing new formed PVC chains and their primary aggregates occur in the later polymerization stage.