Abstract:Using the method of bulk reactive extrusion radical copolymerization, N -phenyl maleimide ( N -PMI) and styrene (St) and methyl methacrylate (MMA) were copolymerized. Through multi-detection gel permeation chromatography, bulk copolymerization kinetic analysis, UV-Vis spectroscopy, elemental analysis, and 1 H NMR and 13 C NMR analysis, it was found that, contrary to the classical free radical copolymerization theory, N -PMI and MMA could not only achieve copolymerization, but could even reach the level of azeotropic copolymerization. The factor that caused this change turned out to be the viscosity of the system. Secondly, through DSC, TG and GC-MS analysis, it was found that N -PMI units were randomly inserted into the molecular chain of PMMA, which greatly improved the stiffness of its molecular segments and the T g of the copolymer; at the same time, the insertion of N -PMI units also very effectively blocked the zipper-style de-end group degradation that often occurs in PMMA. When the mass content of the N -PMI copolymer reached 10%, the T g , initial degradation temperature and semi-degradation temperature of the copolymer increased by 19 °C, 58 °C and 47 °C, respectively. In addition, St, N -PMI can also significantly improve the processing fluidity of the PMMA copolymer, and after St participates were introduced in the copolymerization, the melt flow rate can be increased by 3.5 times. Furthermore, the copolymer not only had good mechanical properties and transparency, but also had excellent antibacterial properties against E. coli and S. aureus with only the effect of trace residual N -PMI in the copolymer. This provides an excellent reference for the preparation of antibacterial PMMA with high heat resistance, good mechanical properties and high transparency.

Mutual Solubility And Bulk Copolymerization Of Vinyl Monomers With N-Substituted Maleimide

Research of Styrene/Aerylonitrille/N-Phenlymaleimide Emalsion Copolymerization

Continuous Thermal Bulk Copolymerization of Styrene and Maleic Anhydride

Semicontinuous thermal bulk copolymerization of styrene and maleic anhydride: Experiments and reactor model

Studies on the Sequence Structure of Vinyl Monomer-N-Phenylmaleimide Copolymers

Copolymerization kinetics of styrene with N-phennyl maleimide in bulk process

Studies on the Microstructure of Vinyl/N-Phenylmaleimide Copolymers by Nmr and Their Applications

Reactivity Ratios and Copolymer Composition of Vinyl Chloride and N-Substituted Maleimide Copolymerization

Study on Suspension Copolymerization Rate of Vinyl Chloride/n-Phenylmaleimide

Kinetics of N-Phenlymaleimide/Styrene/Acrylonitrile/ɑ-Methylstyrene Emulsion Copolymerization

Principle and Application of Composition Distribution Measurement for Vinyl s/N-Phenyl mai eimide Copolymer

Effects of Water Solubility of Monomer on the Kinetics of Methyl Methacrylate Suspension Polymerization

Control and Optimization for Vinyl Chloride/N-Phenylmaleimide Copolymer Composition

Marriage of Ring-Opening Metathesis Polymerization and Thiol-Maleimide Chemistries: Direct Polymerization of Prefunctionalized Monomers or Postpolymerization Modification?

Prediction, Control and Optimization for Vinyl Monomer/N-Phenylmaleimide Copolymers Composition

Measurement and model of molecular weight for Styrene/N-Phenyl maleimide copolymer

Studies on the Self-Condensing Vinyl Polymerization of A Novel Maleimide Inimer

Atom transfer radical copolymerization of methyl methacrylate withN-cyclohexylmaleimide

Radical reaction extrusion copolymerization mechanism of MMA and N-phenylmaleimide and properties of products

Synthesis and Characterization of Heat‐resistant N‐phenylmaleimide–styrene–maleic Anhydride Copolymers and Application in Acrylonitrile–butadiene–styrene Resin

Stability Of Emulsifier-Free Emulsion Copolymerization Of Methyl Methacrylate/Butyl Acrylate/Sodium Mono(Ethyl Polyoxyethylene)Maleate