Mechanical Properties of a Novel Tungsten Fiber-Reinforced Tungsten Composite Prepared Through Powder Extrusion Printing and High-Pressure High-Temperature Sintering
Tianyu Zhao,Jialin Li,Jun Tang,Jiming Chen,Xiang Liu,Qiang Tao,Zhaodong Liu,Jiaen Cheng,Pinghuai Wang,Juan Du
DOI: https://doi.org/10.1016/j.nme.2023.101553
IF: 3.037
2023-11-12
Nuclear Materials and Energy
Abstract:Tungsten is one of the most promising candidate materials for plasma-facing materials (PFM) because of its high melting point, superior thermal conductivity, and low sputtering rate. However, its significant brittleness and high ductile-to-brittle transition temperature constrain its broader engineering applications. To address these limitations, we developed a novel tungsten fiber-reinforced tungsten (W f //W) composite. This composite utilizes commercially available black tungsten wire mesh as the fiber reinforcement phase with a mass ratio of 1%. The material was synthesized through a combined Powder Extrusion Printing and High-Pressure, High-Temperature sintering process, achieving a relative density exceeding 99%. Additionally, the composite exhibits a maximum hardness of 589±10 HV, attributable to the presence of high-density dislocations in the matrix. Its compressive strength reaches up to 1530 MPa, and the plastic deformation strain is as high as 15.8%, both of which are outstanding compared to existing research. These findings offer an alternative route for producing high-density W f //W materials, in addition to chemical vapor deposition method and powder metallurgy technique.
nuclear science & technology