Identification of Metastable Rod-Like Particles in an Isothermally Aged Al-10mg-0.5ag (mass%) Alloy

M Kubota,JF Nie,BC Muddle
DOI: https://doi.org/10.2320/matertrans.46.1288
2005-01-01
MATERIALS TRANSACTIONS
Abstract:The structure and morphology of a precipitation product in an Al-10Mg-0.5Ag (mass%) alloy aged isothermally at 240 C have been characterised using transmission electron microscopy and microbeam electron diffraction. A metastable T phase (Mg32Al, Ag-49, b.c.c. a = 1.41 nm) which is identified by the electron microdiffraction patterns, has been found in the Al 10Mg 0.5Ag (mass%) alloy after solution treatment, water quenched and then aged for 2h at 240 C. The orientation relationship between the T phase and matrix alpha Al phase was of the form (010)(T) parallel to(111)(alpha) and [001](T) parallel to [110](alpha). Qualitative microanalysis suggested that the metastable crystalline T phase was a ternary compound that contained all three elements Al, Mg and Ag. The morphology of the metastable T phase is the (110)(alpha) rod like in shape and those precipitate particles are homogeneously nucleated, and tinely and uniformly dispersed in the Al matrix. The icosahedral quasicrystalline phase was observed in the early stages of ageing (0.5 h at 240 C), and it was to be replaced by the metastable crystalline T phase Mg32Al, Ag-49 after the alloy is aged for 2h at 240 C. The T phrase formed as faceted rods parallel to < 110 >(alpha) directions of the alpha.Al matrix appeared to be the primary strengthening constitute exhibiting maximum hardness in the Al-10Mg-0.5Ag (mass%) alloy at 240 C.
What problem does this paper attempt to address?