Aging of an Al-Mg-Si Alloy with a Silicon Excess and Reinforced with Ceramic Particles

G. Meyruey,V. Massardier,M. Perez

DOI: https://doi.org/10.1007/s11661-020-05736-x

2020-04-09

Metallurgical and Materials Transactions A

Abstract:The aging of an Al-Mg-Si alloy with a high silicon excess and reinforced with ceramic particles was characterized between 373 K and 623 K to understand how the particles affect: (i) the precipitation kinetics of coherent and semi-coherent phases, (ii) the precipitation sequence of the alloy, and (iii) the loss of mechanical strength from a peak-aged microstructure obtained by a T6 treatment. Compared with the unreinforced alloy, heterogeneous precipitation of disordered semi-coherent phases occurs on dislocations and the precipitation kinetics were found to be accelerated in the composite leading to an acceleration of the loss of strength from the T6 condition, due to the precipitation of the Type-C phase. An experimental isothermal transformation curve was proposed for the composite and compared with that of the unreinforced alloy. Then, a study was performed on a deformed alloy to demonstrate that most of the differences observed between the unreinforced alloy and the composite can be explained by the high dislocation density generated in the matrix of the composite due to the presence of ceramic particles. Lastly, the decrease in mechanical strength occurring during isothermal treatments from the T6 state could be successfully modeled using the JMAK approach.