Abstract:The propagation behavior of threading dislocations (TDs) and the effects of Burgers vectors in hydride vapor phase epitaxy (HVPE) GaN bulk crystals generated on Na-flux-grown GaN and in a commercially available HVPE-grown GaN bulk crystal were investigated. Analyses based on chemical etching and transmission electron microscopy (TEM) revealed a close correlation between the etch pit sizes and the Burgers vector of these TDs. The existence of TDs with the unique Burgers vector b = 1m + 1c was observed for the first time ever using a large-angle convergent-beam electron diffraction technique and plan-view bright-field scanning TEM. Multi-photon excitation photoluminescence microscopy observations showed that TDs with b = 1c had a meandering morphology in contrast to the linear morphology of TDs with b = 1a, 1a + 1c, or 1m + 1c in both types of HVPE-grown GaN crystals. The inclinations of TDs with b = 1a and 1a + 1c in HVPE-grown GaN on Na-flux-grown GaN were greatly affected by large symmetrical hexagonal hillocks. The TDs with b = 1a were inclined in the slope directions of the hillock planes, while those with b = 1a + 1c were inclined in the a directions parallel or antiparallel to the a component in their Burgers vector. These inclinations were readily explained by the isotropic elastic theory of an individual TD. The hillocks were produced around pairs of parallel mixed TDs for which the a components were opposite to one another. This phenomenon was attributed to inclusions at the interface between the Na-flux-grown GaN substrate and the HVPE-grown layer. The origins of other TDs including unusual ones having b = 1m + 1c are also discussed herein.

Dislocations formed under longitudinal stress field in epitaxial-lateral-overgrowth GaN

Band-edge Emission Enhancement by Longitudinal Stress Field in GaN

Dislocation Evolution in Anisotropic Deformation of GaN under Nanoindentation

Reduction of Dislocations in GaN Epilayer Grown on Si (111) Substrates Using a GaN Intermedial Layer

Dislocation Reduction in GaN on Sapphire by Epitaxial Lateral Overgrowth

Identification of dislocation characteristics in Na-flux-grown GaN substrates using bright-field X-ray topography under multiple-diffraction conditions

Structural Properties of Laterally Overgrown Gan

Dislocation Analysis of InGaN/GaN Quantum Dots Grown by Metal Organic Chemical Vapor Deposition

Spatially Resolved and Orientation Dependent Raman Mapping of Epitaxial Lateral Overgrowth Nonpolar A-Plane GaN on R-Plane Sapphire.

Weak-Beam Thickness-Fringe Contrast Analysis of Defects in GaN Pyramids

Lattice Images of Dislocations with Edge Components in Gan Epilayers Grown on Al2o3 Substrates

Dislocation Slip Behaviors in High-Quality Bulk GaN Investigated by Nanoindentation

Spatial Variation of Electrical Properties in Lateral Epitaxially Overgrown Gan

High-Spatial-Resolution Strain Measurements by Auger Electron Spectroscopy in Epitaxial-Lateral-Overgrowth Gan

Influence of Lateral Growth on the Optical Properties of GaN Epitaxial Layers

Optical Properties Evolution of GaN Film Grown Via Lateral Epitaxial Overgrowth

Propagation of threading dislocations and effects of Burgers vectors in HVPE-grown GaN bulk crystals on Na-flux-grown GaN substrates

Role of threading dislocation structure on the x‐ray diffraction peak widths in epitaxial GaN films

Piezoelectric field, exciton lifetime, and cathodoluminescence intensity at threading dislocations in GaN{0001}

Strain Effects On Auger Electron Spectroscopy In Different Regions Of Epitaxial-Lateral-Overgrowth Gan

Study of different type of dislocations in GaN thin films