Abstract:A novel Nafion/SiO2 nanocomposite membrane has been developed by combining the self-assembly route and Nafion/SiO2 hybrids. Nafion-stabilized SiO2 nanoparticles were synthesized by using the self-assembly route. The hydrolysis procedure has significant influence on the size and distribution Of SiO2 nanoparticles and the quality and performance of the composite membranes. Best results were obtained on the Nafion/SiO2 composite membrane recast from Nafion-SiO2 (5 wt %) nanoparticles with a H2O:TEOS ratio of 4:1. The Nafion/SiO2 composite membrane prepared by the self-assembled Nafion-Si02 nanoparticles shows remarkable durability as compared to the Nafion/SiO2 Composite membrane prepared by the conventional sol-gel method and pure Nafion 212 membrane, most likely due to the intimate interface between the self-assembled Nafion-Si02 nanoparticles and Nafion polymeric matrix. The tensile strength and proton conductivity of the self-assembled Nafion/SiO2 nanocomposite membranes are 27.5 MPa and 0.090 S/cm, respectively, close to that of the pure Nafion 212 membrane. The lambda O-H2/SO3H of the self-assembled Nafion/SiO2 composite membrane at 60 degrees C is 7.02, similar to 5 times higher than 1.33 of the Nafion 212 membrane. Very different from the pure Nafion 212 membrane, the PEM fuel cells assembled with a self-assembled Nafion/SiO2 nanocomposite membrane show good performance and negligible performance decay when the RH of the inlet gases changes from 100% to 50% under a constant current load of 600 mA cm(-2) at 60 degrees C. This work demonstrates the promising potential of the self-assembled Nafion/SiO2 Composite membranes for the development of high-performance and high-stability PEM fuel cells with high tolerance to RH variations at elevated high temperatures.

Preparation of a self-humidifying membrane electrode assembly for fuel cell and its performance analysis

Novel-SiO2-Doped Proton Exchange Membrane for Self-Humidifying Fuel Cell

An Ultrathin Self-Humidifying Membrane for PEM Fuel Cell Application: Fabrication, Characterization, and Experimental Analysis

Preparation of nano-porous SiO2-gel and its application in proton exchange membrane fuel cell

A novel preparation for a self-humidifying membrane electrode assembly and performance of its fuel cell

Interfacial Water Management of Gradient Microporous Layer for Self-Humidifying Proton Exchange Membrane Fuel Cells

A Novel Ptfe-Reinforced Multilayer Self-Humidifying Composite Membrane for Pem Fuel Cells

Development of novel self-humidifying composite membranes for fuel cells

Effect of doping SiO2 on PEMFC performance at low humidity

Preparation of a Novel Silica Gel for Electrode Additive of PEMFCs

Study of Novel Self-Humidifying PEMFC with Nano-TiO2-Based Membrane

Membrane Electrode Assembly with Pt/SiO2/C Anode Catalyst for Proton Exchange Membrane Fuel Cell Operation under Low Humidity Conditions

Composite Membranes from Quaternized Chitosan Reinforced with Surface-Functionalized PVDF Electrospun Nanofibers for Alkaline Direct Methanol Fuel Cells

Preparation of novel nano-SiO2-gel additive and performance of PEM fuel cell

Control Mechanism of a Modified Buffer Layer on Interfacial Mass Transfer Efficiency for a Proton Exchange Membrane Fuel Cell at Varying Humidity

Preparation and evaluation of a novel self-humidifying Pt/PFSA composite membrane for PEM fuel cell

Self-humidification of a PEM fuel cell using a novel Pt/SiO2/C anode catalyst

Study of Novel Self-Humidifying PEMFC with Nano-TiO<sub>2</sub>-Based Membrane

More Sustainable Electricity Generation in Hot and Dry Fuel Cells with a Novel Hybrid Membrane of Nafion/nano-silica/hydroxyl Ionic Liquid

Synthesis and Characterization of a Self-Assembled Nafion/Silica Nanocomposite Membrane for Polymer Electrolyte Membrane Fuel Cells