Layered Double Hydroxide-Coated Silica Nanospheres with 3D Architecture-Modified Composite Anion Exchange Membranes for Fuel Cell Applications

Shujun Zhao,Wen-Chin Tsen,Fuqiang Hu,Fei Zhong,Hai Liu,Sheng Wen,Genwen Zheng,Caiqin Qin,Chunli Gong

DOI: https://doi.org/10.1007/s10853-019-04178-0

IF: 4.5

2019-01-01

Journal of Materials Science

Abstract:A flower-like hierarchical structure consisting of a hydroxide ion conductor (layered double hydroxide, LDH) wrapped on hydrophilic SiO 2 nanospheres (LDH@SiO 2 ) was first prepared by an in situ co-precipitation method and then quaternized. This resulting nanocomposite (QLDH@SiO 2 ) was used as a multifunctional additive to modify a quaternized chitosan/polyvinyl alcohol (QCS/PVA) blend matrix to prepare composite membranes. The surface modification of LDH@SiO 2 with the silane coupling agent facilitates its dispersion within the blend matrix, which leads to the decreased degree of crystallinity and significant enhancement of mechanical properties of the composite membranes. Furthermore, in situ vertical growth of LDH on the surface of SiO 2 cores can effectively avoid the ab-face stacking aggregation of LDH, which can take full advantage of the intrinsic hydroxide-conducting ability of LDH nanosheets. Compared to the ion exchange capability (only 2.09 mmol g −1 ) and effective ionic mobility (1.23×10 −5 cm 2 s −1 V −1 ) of the pristine membrane, the two values for the composite membrane containing 6 wt% of QLDH@SiO 2 increased to 2.63 mmol g −1 and 1.50×10 −5 cm 2 s −1 V −1 , respectively. In alkaline direct methanol fuel cell tests at 60 °C, the QCS/PVA-6% QLDH@SiO 2 composite membrane demonstrates peak power density of 64 mW cm −2 which is 82% higher than that of the pristine membrane (only 35 mW cm −2 ). Moreover, the increased alkaline stability and decreased methanol permeability of the composite membranes also guarantee their satisfactory fuel cell stability.