Novel Silica/poly(2,6-Dimethyl-1,4-phenylene Oxide) Hybrid Anion-Exchange Membranes for Alkaline Fuel Cells: Effect of Silica Content and the Single Cell Performance

Yonghui Wu,Cuiming Wu,John R. Varcoe,Simon D. Poynton,Tongwen Xu,Yanxun Fu

DOI: https://doi.org/10.1016/j.jpowsour.2009.11.118

IF: 9.2

2010-01-01

Journal of Power Sources

Abstract:Poly(2,6-dimethyl-1,4-phenylene oxide) (PPO)-based organic–inorganic hybrid alkaline membranes with enhanced hydroxyl (OH−) conductivity are prepared in response to the relatively low conductivity of previously reported PPO-based systems. The membranes also exhibit higher swelling-resistant properties and the hydroxyl (OH−) conductivity values are comparable to previously reported fluoropolymer-containing membranes: 0.012–0.035 S cm−1 in the temperature range 30–90 °C. Other favorable properties for fuel cell application include high tensile strengths up to 25 MPa and large ion-exchange capacities in the range 2.01–2.27 mmol g−1. Beginning-of-life fuel cell testing of a membrane with a thickness of 140 μm yielded an acceptable H2/O2 peak power density of 32 mW cm−2 when incorporated into an alkaline membrane electrode assembly. Therefore, this class of hybrid membrane is suitable for application in alkaline membrane fuel cells.