Abstract:Bulk glassy Cu–Zr–Ti base alloys containing a small amount of Nb or Ta were found to exhibit high strength combined with significant plastic elongation. The glass transition temperature (Tg), crystallization temperature (Tx) and ΔTx(=Tx−Tg) of the Cu-based bulk glassy alloys are in the range of 719 to 731 K, 765 to 769 K and 46 to 44 K, respectively, for the Nb-containing alloy and 716 to 741 K, 752 to 780 K and 44 to 34 K, respectively, for the Ta-containing alloy. With increasing Nb or Ta content to 3 at% for the (Cu0.6Zr0.3Ti0.1)100−xMx alloys, the Young’s modulus, yield strength and compressive fracture strength increase from 114 to 121 GPa, 1785 to 2010 MPa and 2150 to 2250 MPa, respectively, and the plastic elongation shows a maximum of 1.8% at 1%Nb and 3.4% at 1%Ta. The 1%Ta alloy exhibited good combination of high fracture strength of 2250 MPa and large total elongation of 5.4%. The effectiveness of additional Nb or Ta on the increase in elongation and fracture strength is presumably due to the mixed state of atomic pairs with attractive and repulsive bonding natures among the constituent elements with significantly different atomic size mismatches. The success of forming the bulk glassy alloys with high strength and significant elongation is encouraging for future applications as high-strength type materials.

Formation, Thermal Stability, Mechanical Properties and Corrosion Resistance of Cu-Zr-Ti-Ni-Nb Bulk Glassy Alloys

Formation, Thermal Stability and Mechanical Properties of Zr-Nb-Cu-Ni-Al Bulk Metallic Glasses

Glass formation, corrosion behavior and mechanical properties of bulk glassy Cu–Hf–Ti–Nb alloys

Glass-forming ability and corrosion resistance of Zr-based Zr-Ni-Al bulk metallic glasses

Thermal Stability and Mechanical Properties of Bulk Glassy Cu-Zr-Ti-(Nb, Ta) Alloys

Formation of Ni–Nb–Zr–X (X = Ti, Ta, Fe, Cu, Co) Bulk Metallic Glasses

Formation and mechanical properties of bulk Cu-Ti-Zr-Ni metallic glasses with high glass forming ability

Glass Forming Ability and Mechanical Properties of New Ni-Based Bulk Metallic Glasses

High-strength Cu-based bulk glassy alloys in Cu–Zr–Ti and Cu–Hf–Ti ternary systems

Preparation of (ti0.45cu0.378zr0.10ni0.072)100−xsnx Bulk Metallic Glasses

Cu-Based Bulk Glassy Alloys with Good Mechanical Properties in Cu-Zr-Hf-Ti System

Cu-based bulk glassy alloys with high tensile strength of over 2000 MPa

Tuning Glass Formation and Mechanical Properties of ZrCoAl(Nb) Bulk Metallic Glass with Nb Microalloying Process

Formation, Thermal Stability and Mechanical Properties of Ti42.5Zr7.5Cu40Ni5Sn5 Bulk Metallic Glass

Unusual Solidification Behavior of a Zr–Cu–Ni–Al Bulk Glassy Alloy Made from Low-Purity Zr

Glass-forming Ability and Thermal Stability of a New Bulk Metallic Glass in the Quaternary Zr–Cu–Ni–Al System

A Novel Ni-Free Zr-Based Bulk Metallic Glass with High Glass Forming Ability, Corrosion Resistance and Thermal Stability

Corrosion behavior, mechanical properties and cell cytotoxity of Zr-based bulk metallic glasses

Preparation And Thermal Stability Of Zr-Al-Ni-Cu-Nb Bulk Amorphous Alloy Matrix Composites

Composition Dependence of the Microstructure and Mechanical Behavior of Ti–Zr–Cu–Pd–Sn–Nb Bulk Metallic Glass Composites

High Tensile Plasticity and Strength of a CuZr-based Bulk Metallic Glass Composite