Abstract:This work highlights the relationship between the preparation, crystallization behavior, microstructures, and mechanical properties of Cu-based bulk metallic glasses (BMGs) and their composites (BMGCs). (Cu47Zr45Al8)97.5Y1.5Nb in-situ BMGCs were prepared using isothermal annealing, and the experimental results indicate tunable mechanical properties of the alloys by processing parameter manipulation. The crystallinity of (Cu47Zr45Al8)97.5Y1.5Nb BMGCs increases with extended annealing temperature and time, while their phase transition with rising temperature follows Am (amorphous state) → Am + Cu10Zr7 →Am + Cu10Zr7 + AlCu2Zr + Al2Zr. Precipitation strengthening during annealing above 720 K (447 ºC) can enhance the alloy microhardness remarkably and achieve an optimum of 712 HV by annealing at 800 K (527 ºC) for 60 min. TEM results show that Cu10Zr7 with sizes of 12~15 nm precipitates out upon crystallization and thereby accounts for the superior compressive property. The alloy exhibits a fracture strength up to 2080 MPa after annealing at 680 K (407 ºC) for 30 min. Morphological observation of the fracture surface reveals a transition of fracture characteristics from the typical amorphous ductile manner to a brittle manner with further annealing. The investigation provides novel thoughts of BMGs processing for further performance improvement.

High Tensile Plasticity and Strength of a CuZr-based Bulk Metallic Glass Composite

Enhanced Plasticity in a Zr-based Bulk Metallic Glass Containing Nanocrystalline Precipitates

Incorporation of ultrafine nanograins in Zr–Cu–Al–Ni–Co bulk metallic glass enabling significantly improved mechanical properties

Concurrently achieving strength-ductility combination and robust anti-wear performance in an in-situ high-entropy bulk metallic glass composite

New Class of Plastic Bulk Metallic Glass.

Plasticity-improved Zr–Cu–Al Bulk Metallic Glass Matrix Composites Containing Martensite Phase

Substantially enhanced plasticity of bulk metallic glasses by densifying local atomic packing

Improved Tensile Ductility by Severe Plastic Deformation for Nano-Structured Metallic Glass.

Effects of Cu Additions on Mechanical and Soft-Magnetic Properties of CoFeBSiNb Bulk Metallic Glasses

Crystallization Behavior and Mechanical Properties of Cu-based Bulk Metallic Glass Composites

Heterogeneous metallic glass composites with a unique combination of strength, plasticity and conductivity

Enhancing strength and plasticity of Zr-based bulk metallic glasses by Zr partially substituted Fe and isothermal annealing

A Plastic Zr–Cu–Ag–Al Bulk Metallic Glass

Enhanced mechanical properties of Zr65Cu15Ni10Al10 bulk metallic glass by simultaneously introducing surface grooves and multiple shear bands

Development of High Strength Ni–Cu–Zr–Ti–Si–Sn In-Situ Bulk Metallic Glass Composites Reinforced by Hard B2 Phase

Enhancement of Plasticity in Zr-based Bulk Metallic Glasses

Cryogenic thermal cycling induced simultaneous improvement of strength and ductility in a Zr-based bulk metallic glass composite

Deformation-induced microstructural heterogeneity and rejuvenation in a Zr-based bulk metallic glass

Formation and mechanical properties of bulk Cu-Ti-Zr-Ni metallic glasses with high glass forming ability

Determining deformation behaviors in a CuZr-based bulk metallic glass composite

Enhancing strength-ductility synergy in an ex situ Zr-based metallic glass composite via nanocrystal formation within high-entropy alloy particles