Abstract:The (1−x)ZnWO4–xTiO2 composite ceramics were synthesized by the conventional solid-state method. The phase formation, microstructures, element composition and microwave dielectric properties of (1−x)ZnWO4–xTiO2 composite ceramics and 0.75ZnWO4–0.25TiO2 ceramics with Li2CO3–H3BO3 addition were investigated. Biphase structure of (1−x)ZnWO4–xTiO2 composite ceramics sintered at 1160°C/2h was confirmed by using X-ray diffraction and the back scattering electron images. The dielectric constant εr and the temperature coefficient of resonant frequency τf values of composite ceramics increased linearly with the increase of TiO2 phase. The τf value of (1−x)ZnWO4–xTiO2 was found to be dependent on phase composition, which is related to the amount of TiO2. When x is 0.25, the τf value of (1−x)ZnWO4–xTiO2 was near 0ppm/°C. With small amount of Li2CO3–H3BO3 addition, the sintering temperature of composite ceramics was further reduced to below 950°C from about 1100°C without obviously deteriorating the microwave dielectric properties, and the τf values could be adjusted with the Li2CO3–H3BO3 content. The 0.75ZnWO4–0.25TiO2 ceramics with 5.0wt% Li2CO3–H3BO3 sintered at 950°C/2h exhibited good microwave dielectric properties of εr=18.99, Q×f=13,517GHz and τf=−11.44ppm/°C.

Synthesis and Characterization of (zn,co)tio3 by Modified Low Temperature Preparing Route

Preparation and Properties of CaTiO_3:Zn Nanoparticles Based on Sol-Gel Method

The Characterization and Preparation of Nano-Scale Fe Doping Tio2 by Sol-Gel Method (I) - the Crystallization and Thermal Decomposition Process of Fe Doping Tio2 Xerogel Powders Using Thermal Tg-Ir Spectrometry

Synthesis of ZnTiO3 Ceramic Powders by Sol-Gel Method

Synthesis, formation and characterization of ZnTiO3 ceramics

Microstructure and Microwave Dielectric Properties of Tio2-Doped Zn2sio4 Ceramics Synthesized Through the Sol-Gel Process

Synthesis of Pb(Zr0.52Ti0.48)O3(PZT) Powder by A Partial Lead Oxalate Coprecipitation Method

Solid-phase Synthesis and Characterization of ZnO-TiO 2 System

Formation and Transformation of Cubic ZnTiO3 Powders Prepared by Sol-gel Process

Microwave Dielectric Properties of Low Temperature Sintered ZnWO4–TiO2 Composite Ceramics

Characterization of ZnTiO 3 powders prepared by sol-gel process

Hydrothermal synthesis and characterization of (Zr1−xSnx)TiO4 (x = 0.05–0.20) powders

Investigation on the Synthesis of (zn1−xmgx)tio3 and the Modulation Effect of CaTiO3

Preparation and Dielectric Properties of (ca0.61,nd0.26)tio3 Nanoparticles by a Sol–gel Method

Preparation and Characterization of Pb(Zr0.52Ti0.48)O3 Ultrafine Powders by a Sol-Gel Combined with Combustion Process

Phase transitions of low-temperature sintering tungsten-doped ZnO-TiO 2 ceramics

Co 2 O 3 substitution effects on the structure and microwave dielectric properties of low-firing (Zn 0.9 Mg 0.1 )TiO 3 ceramics

Preparation of pure MgTiO3 powders and the effect of the ZnNb2O6-dope onto the property of MgTiO3-based ceramics

Synthesis and Dielectric Properties of ZnNb2O6/TiO2 Sintered at Low Temperature

Formation and transformation of ZnTiO3 prepared by sol–gel process

Investigation on the synthesis of (Zn 1−x Mg x )TiO 3 and the modulation effect of CaTiO 3