Surface Strengthening of Ti3SiC2 Through Magnetron Sputtering of Mo and Zr and Subsequent Annealing

Haiping Guo,Aijun Li,Jie Zhang,Lingfeng He,Yanchun Zhou

DOI: https://doi.org/10.1016/j.jeurceramsoc.2009.04.042

IF: 5.7

2010-01-01

Journal of the European Ceramic Society

Abstract:Magnetron sputtering deposition of Mo and Zr and subsequent annealing were conducted with the motivation to modify the surface hardness of Ti3SiC2. For Mo-coated Ti3SiC2, Si diffused outward into the Mo layer and reacted with Mo to form molybdenum silicides in the temperature range of 1000–1100°C. The MoSi2 layer, however, cracked and easily spalled off. For Zr-coated Ti3SiC2, Si also diffused outward to form Zr–Si intermetallic compounds at 900–1100°C. The Zr–Si compounds layer had good adhesion with Ti3SiC2 substrate, which resulted in the increased surface hardness.