Abstract:Thermal decomposition was the prerequisite and basis for the utilization of magnesite resources. However, the calcination of magnesite was usually accompanied by high energy consumption, which not only caused serious waste of magnesite resources, but also restricted its high value-added utilization. Therefore, calcination conditions were the key to controlling thermal decomposition process of magnesite. The kinetics of high-grade magnesite thermal decomposition was elaborated by non-isothermal thermogravimetric analysis, and meanwhile the effect of heating rate on the magnesite thermal decomposition reaction and morphology of MgO particles were characterized. Both Doyle and Gorbatchev approximate functions were used to simulate the magnesite thermal decomposition process, where the experimental data (correlation coefficient) fitted by the latter could obtain more acceptable kinetic parameters of the magnesite thermal decomposition. The good linear relationship between the activation energy and the pre-finger factor allowed for a kinetic compensation of the thermal decomposition of magnesite. Furthermore, higher heating rate induced the formation of terraced grains, grain network group, cubic grains, and spherical grains for the samples sintered at 1200 degrees C. The heating rate largely affected the magnesite particle morphology, grain size distribution and activity, and also provided important technical indicators in the actual production of magnesia refractory raw materials.

The Research of Magnesium Extracted from Low-Grade Magnesite by Ammonium Sulfate Calcining Method and the Reaction Kinetics

Kinetics of Leaching Lightly Calcined Magnesia with (NH4)2SO4

Non-isothermal kinetic study of high-grade magnesite thermal decomposition and morphological evolution of MgO

Novel Calcining Process of Low-grade Magnesite

Preparation of Active Magnesia with Magnesite

Preparation of High-Purity Magnesia by Carbon Monoxide Reduction Pyrolysis of Magnesium Sulfate

Preparation of High-Purity Magnesia by Solid Phase Reduction Decomposition of Magnesium Sulfate

Evaluation on Hydration Reactivity of Reactive Magnesium Oxide Prepared by Calcining Magnesite at Lower Temperatures

Study on the Process of the Preparation of Activated MgO by Calcining Magnesite

Development and Characterization on the Isothermal Kinetics of Mg(OH)2-sol Synthesized by Chemical Method

Effect of MgO Calcination Temperature on the Reaction Products and Kinetics of MgO–SiO2–H2O System

Preparation of nano-sized magnesia with industrial oxalic acid and magnesium hydroxide

Performance Variations of Light Burned Magnesia under Different Calcination Parameters and Its Effects on Magnesium Oxysulfate Cement Preparation

Dynamic study on desulphurization reaction of MgO-CaO refractories

Improvement of utilization efficiency of magnesite by (NH4)2SO4 roasting–water leaching process

Preparation of Ccalcining MgO and its precursor

Investigation on Preparation of Anhydrous Magnesium Chloride by Ammonia Complexation Method

Preparation of MgO with low CaO content and high specific surface area from low-grade dolomite

Improvement on the Processes of MgO Manufacture

Study on the thermal decomposition mechanism of Mg(NO3)2·6H2O from the perspective of resource utilization of magnesium slag

Mass Transfer and Reaction Kinetics in the Carbonization of Magnesium Oxide from Light Calcined Magnesia with Mechanical Force Enhancement