Abstract:To promote the innovation of raw magnesium production technology, an integrated calcination and silicothermic reduction short process for magnesium production was experimentally studied on the laboratory scale in this article. The influences of the thermal decomposition temperature, silicothermic reduction temperature, pelletizing pressures and silicon ratio on the characteristics of producing the magnesium by the short process was studied. The crosslinking effect, including reactions between CO2 decomposed from dolomite and metal elements in ferrosilicon, microstructure change at thermal decomposition and silicothermic reduction stages, was analyzed and discussed. In addition, comparison of the magnesium reduction rate and production efficiency between the new short process and the traditional Pidgeon process was made. The results indicated that the decomposition and reduction temperatures have a more significant influence on the magnesium reduction process than the pelletizing pressure and silicon ratio. A decomposition temperature < 1000 °C and reduction temperature > 1100 °C was proven to be favorable for improving the magnesium reduction rate and production efficiency of the new short process. It was also found that the integrated short process for magnesium production can reach the same total reduction rate and has lower efficiency compared to the traditional process. The decrease of magnesium production efficiency in the new short process was expected to result from reduction of the contact area and hindering of diffusion between CaO·MgO molecules and Si(Fe) atoms because of the microstructure change and ferrosilicon consumption by the reactions between CO2 and metal elements in ferrosilicon. Preparing briquettes with additives of binder or ultrafine particles of raw materials was proposed and considered for further study to improve the production efficiency.

Novel Calcining Process of Low-grade Magnesite

Preparation of calcium carbonate and nesquehonite (MgCO3·3H2O) from low-grade magnesite

Study on Industrial Application of a Low Grade and High Calcium Magnesite Separation Technology

Non-isothermal kinetic study of high-grade magnesite thermal decomposition and morphological evolution of MgO

Preparation of Active Magnesia with Magnesite

Experimental Study of Magnesium (Mg) Production by an Integrated Calcination and Silicothermic Reduction Short Process

Study on the Process of the Preparation of Activated MgO by Calcining Magnesite

Effect of La2O3 addition on the microstructural evolution and thermomechanical property of sintered low-grade magnesite

Study of Carbonizing Processes for Sintered Dolomite

Utilization of Coal Gangue and Copper Tailings As Clay for Cement Clinker Calcinations

Research on the Phase Transformation in Calcification - Carbonation Method for Low-Grade Bauxite Utilization

Preparation of Ccalcining MgO and its precursor

Single-step conversion of low-grade magnesite to anhydrous MgCO 3 based on a biodegradable salicylic acid chelating system: Characterization; DFT calculations; mechanism

Evaluation on Hydration Reactivity of Reactive Magnesium Oxide Prepared by Calcining Magnesite at Lower Temperatures

Preparation and Characterization of Microporous Magnesia‐based Refractory

Mechanism of CaO in Light-Burned Magnesia on the Formation Process, Mechanical Properties, and Water and Chloride Resistance of the 517 Phase

Effect of Calcining Process on Assimilation and Carbonation of Calcined Dolomite Slurry

Preparation of light magnesia by using industrial waste alkali and brine

A novel treatment processes of struvite with pretreated magnesite as a source of low-cost magnesium

Preparation of nano-sized magnesia with industrial oxalic acid and magnesium hydroxide

Calcination Condition of Dolomite‐Based Materials Influencing Static Dissolution in Synthetic Electric Arc Furnace Slag