Abstract:The magnesium sulfate heptahydrate prepared by magnesite and commercial sulfuric acid was dehydrated to prepare anhydrous magnesium sulfate.The high-purity magnesia was obtained by commercial magnesium sulfate and carbon monoxide.The influences of the particles diameter,gas flow,calcining temperature and time on the purity of prepared magnesium oxide were investigated.The optimum processing parameters of precipitation were obtained by single factor experiments,and the conditions were as follows: the grain diameter 51.8 μm,the carbon monoxide flow 30 mL/min,the calcining heat 800 ℃,the calcining time 2.0 h.The morphology of the magnesia was characterized by X-ray diffractometry(XRD) and scanning electron microscopy(SEM).The results indicate that sample particle has high purity to 99%,the average particle diameter is 40 nm.The single molecule surface with high specific surface area is porous and fluffy.By means of experiment and kinetic deduction,an empirical equation for the calcining process was established,and the apparent activation energy is 234.055 kJ/mol.The calcining process of magnesium sulfate can be simulated with a shrinking core model,which indicates that the control factor of the calcining process is the diffusion rate of reacting reagents in the redox process.

Preparation of High-Purity Magnesia by Solid Phase Reduction Decomposition of Magnesium Sulfate

Preparation of High-Purity Magnesia by Carbon Monoxide Reduction Pyrolysis of Magnesium Sulfate

Study on Preparation of MgO Crystal Whisker from Magnesite

Research on preparation of high purity magnesite from MgCl2·6H2O

Preparation of nano-sized magnesia with industrial oxalic acid and magnesium hydroxide

Preparation of high-purity light magnesia from sulfate salt subtype salt lake brine

Preparation of High-Purity Ultrafine Magnesium Hydroxide Using Solid-State Reaction Method

Preparation of Magnesium Hydroxide Dry Powder by Hydrating Method

Improved Lime Method to Prepare High-Purity Magnesium Hydroxide and Light Magnesia from Bischofite

Preparation of High-Purity Nanosized Magnesium Hydroxide

Preparation of Carnallite and Magnesium Sulfate from Refined Magnesium Slag

Preparation of nano-sized magnesia by brine-dolomite process

Preparation of Active Magnesium Oxide Powder under Different Conditions by Brine-alkali method

Synthesis of Nano Magnesium Oxide from Dolomite via Ammonium Sulfate Leaching

The preparation of high purity MgO and precision separation mechanism of Mg and Ca from dolomite

Preparation of MgO with low CaO content and high specific surface area from low-grade dolomite

Investigation on Preparation of Anhydrous Magnesium Chloride by Ammonia Complexation Method

Preparation of Active Magnesia with Magnesite

Preparation of Ccalcining MgO and its precursor

Study on Preparation of High-purity Magnesia from Brucite

Preparation of Nano-magnesia by Ultrasonic-alcohol-water and Chelate Precipitation Method