Abstract:Parameter effects on the preparation for nanosized particles of magnesium hydroxide from dolomite via carbonation were investigated. The effects of precipitator and reaction temperature on the morphology of the nanosized particles were evaluated. The improvement of surface active agent on the dispersion of the particles was analyzed. The reaction mechanism of the experiment was discussed. The results show that the crystallization of magnesium hydroxide using ammonia as a precipitator is better than that using sodium hydroxide as a precipitator, and the nanosized particles of magnesium hydroxide appear an approximately thin sheet of hexagons with an average particle size of 16 nm. The smaller crystal nuclei of magnesium hydroxide with the thickness of about 5–7 nm and the size of 10–15 nm could be prepared at the reaction temperature of 30 ℃. The crystal nuclei started to grow larger with the disordered arrangement at 50 ℃. The integrated crystalline grains of magnesium hydroxide with the thickness of about 10 nm and the size of 10–20 nm could be prepared at 70 ℃. However, the irregular arrangement could occur at 80 ℃ . In addition, the dispersion of the nanosized crystalline grains of magnesium hydroxide could be improved by using polyethylene glycol (PEG) or sodium dodecyl sulfate (SDS) as surface active agents. Then the thickness of the nanosized particles is 10 nm. The dispersion performance became superior at an optimized amount of PEG of 3.0%. The dispersion was more efficient at the amount of SDS of 4.0% and its size is 20 nm.

Preparation of Nano-magnesia by Ultrasonic-alcohol-water and Chelate Precipitation Method

Study on Preparation of MgO Crystal Whisker from Magnesite

Preparation of Nano-magnesia by Homogeneous Precipitation

Preparation and Application of Nano - Mg2B2O5

The Investigation on Preparation Technology of Nano-magnesia

Preparation of High-Purity Nanosized Magnesium Hydroxide

Preparation of Magnesium Hydroxide Chloride Hydrate Nanowires Using Calcined Dolomite

PARAMETER EFFECTS ON PREPARATION OF NANOSIZED PARTICLES OF MAGNESIUM HYDROXIDE FROM DOLOMITE AND THEIR CHARACTERS

Study on Suspension Graft Polymerization of MMA onto Nano-sized Basic Magnesium Chloride Whisker Surface in Methanol/Water Disperse Medium

Preparation of Nano Magnesium Oxide by Mechanochemical Method Using Magnesium Chloride

Preparation of High-Purity Ultrafine Magnesium Hydroxide Using Solid-State Reaction Method

Preparation of Nano-sized Magnesium Hydroxide from Dolomites by Acid Immersing

Preparation of Nanometer Magnesia with High Surface Area and Study on the Influencing Factors of the Preparation Process

Nanosized MgO Powder Preparation by Homogeneous Precipitation-Post Annealing Method Using Mg(NO3)2·6H2O as Raw Material

Preparation of Magnesia Nanoballs from Dolomite

SYNTHESIS OF NANOMETER MAGNESIA BY SOL- GEL METHOD

The Influence of Processing Conditions for the Preparation of Super-fine Hydroxide Magnesium by Hydrating Method

The effects of solvent and microwave on the preparation of Magnesium Oxide Precursor: The effects of solvent and microwave on the preparation of Magnesium Oxide Precursor

PREPARATION AND SELF-ASSEMBLY OF GLOBAL NANO-PARTICLES OF MgCl_2-CH_3CH_2OH COMPLEX

Preparation of Magnesium Hydroxide Nanoflowers from Boron Mud Via Anti-Drop Precipitation Method

Synthesis and characterisation of magnesium hydrate microspheres