Abstract:Bulk Ti2AlC-Al2O3/TiAl composites were in situ synthesized by vacuum sintering mechanically alloyed Ti-50 at.% Al powders coated with carbon nanotubes (CNTs). The pre-alloyed Ti-50 at.% Al powder was obtained by ball milling Ti and Al powders. The multi-walled carbon nanotubes as the carbon resource were covered on the surface of the pre-alloyed powders by immersing them into a water solution containing the CNTs. A zwitterionic surfactant was used to enhance the dispersion of the CNTs on the powder surface. The samples were cold pressed and sintered in vacuum at temperatures from 950 to 1250 degrees C, respectively. The results show that the reaction of forming Ti2AlC can be achieved below 950 degrees C, which is 150 degrees C lower than in the Ti-Al-TiC system and 250 degrees C lower than for the Ti-Al-C system due to the addition of CNTs. Additionally, the reinforcement of Al2O3 particles was introduced in situ in Ti2AlC/TiAl by the drying process and subsequent sintering of the composite powders. Dense Ti2AlC-Al2O3/TiAl composites were obtained by sintering at 1250 degrees C and exhibited a homogeneous distribution of Ti2AlC, Al2O3 and precipitated Ti3Al particles and a resulting high hardness. (c) 2013 Elsevier B.V. All rights reserved.

Mechanically Activated Low-Temperature Synthesis of Ti2snc

In-situ Synthesis of Nanocrystalline TiC Powders, Nanorods, and Nanosheets in Molten Salt by Disproportionation Reaction of Ti(II) Species

Effect of Sn and Si on the Synthesis of Ti<sub>3</sub>Al(Sn/Si)C<sub>2</sub> by Self-Propagating High-Temperature Sintering

Low-temperature instability of Ti2SnC: A combined transmission electron microscopy, differential scanning calorimetry, and x-ray diffraction investigations

Preparation of Ti2SnC by Solid—liquid Reaction Synthesis and Simultaneous Densification Method

In Situ Synthesis of Ti2AlC–Al2O3/TiAl Composite by Vacuum Sintering Mechanically Alloyed TiAl Powder Coated with CNTs

Mechanosynthesis Mechanism of Tic Powders

Ti2SnC MAX Phase Directly Synthesized by High-Temperature Ball Milling

Synthesis of Fine Grain Ti3sic2 by Spark Plasma Sintering with Additive of Aluminum

Synthesis of Stoichiometric Titanium Carbide by a Combination of Carbothermal Reduction and Molten Salt Method and Its Characterization

Synthesis Of High-Purity Powder Ti3alc2 Materials By Pressureless Sintering

Phase Assembly of Ti<sub>2</sub>SnC Powders

A novel simple method to stably synthesize Ti3AlC2 powder with high purity

Phase Assembly of Ti2SnC Powders

Fabrication of high purity Ti3SiC2 from Ti/Si/C with the aids of Al by spark plasma sintering

Low-temperature Synthesis of Nano-Sized TiC Particles by Ultrasound Assisted Melt-Reaction of Al-K2TiF6-C System

Synthesis of Submicrometer-Sized TiC Particles in Aluminum Melt at Low Melting Temperature

Microstructure and wear properties of TiC-Al composite fabricated by field activated and low-pressure assisted combustion synthesis

Reactive Synthesis of Polycrystalline Ti3AlC2 and Its Sintering Behavior

Synthesis of Ti3SiC2 Powder by Mechanical Alloying and Mechanical Property of the Sintered Compacts.