Abstract:Samples of aluminum were prepared using spark plasma sintering from a mixture of coarse (average particle size of 6 mu m) and fine (average particle size of 1 mu m) powders to achieve a heterogeneous transmodal grain size distribution covering a range of grain sizes from approximate to 1 to 10 mu m. By careful choice of surface markers both electron back-scatter diffraction (EBSD) data, to track crystal rotations, and digital image correlation (DIC) data, to track local plastic deformation, were collected from the same region during in-situ tensile deformation up to a strain of epsilon t = 0.126. A heterogeneous pattern of crystal rotation is observed for all grain sizes, although in some smaller grains (defined as those <4 mu m diameter) no clear grain sub-division was identified. Plastic strain was more concentrated in the larger grains, but the average rotation rate of the smaller grains was found to be higher than that of larger grains, showing also a much wider spread in rotation rate. Based on the change in average orientation, a clear orientation dependence in the tensile axis rotation direction was observed for many larger grains, in agreement with previously reported data for aluminum with average grain size of 75 mu m, whereas the smaller grains showed a more complex rotation behavior, with more of these grains showing unexpected tensile axis rotations. The combination of both EBSD and DIC during in-situ experiments provides a rich data set for analysis of plastic deformation in samples with a heterogeneous microstructure.

Slip Pattern, Microstructure and Local Crystallography in an Aluminium Single Crystal of Brass Orientation {110}〈112〉

Slip Pattern, Microstructure and Local Crystallography in an Aluminium Single Crystal of Copper Orientation {112}〈111〉

Temperature-Induced Variations in Slip Behavior of Single Crystal Aluminum: Microstructural Analysis

Experimental and Crystal Plasticity Study on Deformation Bands in Single Crystal and Multi-Crystal Pure Aluminium

Evolution Of Microstructure And Local Crystallographic Orientations In Rolled Al-1%Mn Single Crystals Of {001}< 110 > Orientation

On the Origin of Deformation Mechanisms in a Heterostructured Aluminum Alloy Via Slip Trace and Lattice Rotation Analyses

Microstructure and flow stress of polycrystals and single crystals

Orientation dependence of dislocation structure in surface grain of pure aluminium deformed in tension

In-situ Study of the Effect of Strain Path Change on Dislocation Boundary Evolution in Commercial Purity Aluminum

Dislocation Structures In Deformed Metals

Grain Orientation Dependence of Extended Planar Dislocation Boundaries in Rolled Aluminium

Evolution of microstructure and local crystallographic orientations in rolled Al 1% Mn single crystals of {l_brace} 0 0 1 {r_brace}< 1 1 0> orientation

The effect of microstructure on the relationship between grain boundary sliding and slip transmission in high purity aluminum

Strain Distribution and Lattice Rotations During In-Situ Tension of Aluminum with a Transmodal Grain Structure

Microstructure and Texture Evolutions of Aa1050 Aluminum Alloy Cold Rolled to High Strains

Grain Structure and Microtexture Evolution During Superplastic Deformation of 5A90 Al-Li Alloy

In-situ EBSD Study of the Active Slip Systems and Lattice Rotation Behavior of Surface Grains in Aluminum Alloy During Tensile Deformation

Slip initiation in interlayered β and corresponding slip transfer during compression of a lamellar-structure titanium alloy

Evolutions of Grain Orientation and Dislocation Boundary in Aa1050 Aluminum Alloy During Cold Rolling from Low to Medium Strains

Tensile behavior and deformation mechanism for Ti–22Al–25Nb alloy with lamellar O microstructures

Quantifying the Resistance to Dislocation Glide in Single Phase FeCrAl Alloy