Abstract:Three-dimensional (3D) integration technology using Cu interconnections has emerged as a promising solution to improve the performance of silicon microelectronic devices. However, Cu diffuses into SiO2 and requires a barrier layer such as Ta to ensure acceptable reliability. In this paper, the effects of temperature and strain normal to the interface on the inter-diffusion of Cu and Ta at annealing conditions are investigated using a molecular dynamics (MD) technique with embedded atomic method (EAM) potentials. Under thermal annealing conditions without strain, it is found that a Cu-rich diffusion region approximately 2 nm thick is formed at 1000 K after 10 ns of annealing. Ta is capable of diffusing into the interior of Cu but Cu hardly diffuses into the inner lattice of Ta. At the Cu side near the interface an amorphous structure is formed due to the process of diffusion. The diffusion activation energy of Cu and Ta are found to be 0.9769 and 0.586 eV, respectively. However, when a strain is applied, a large number of crystal defects are generated in the sample. As the strain is increased, extrinsic stacking faults (ESFs) and lots of Shockley partial dislocations appear. The density of the dislocations and the diffusion channels increase, promoting the diffusion of Cu atoms into the inner lattice of Ta. The thickness of the diffusion layer increases to 4 times the value when only a temperature load of 700 K is applied. The MD simulations demonstrated that Ta is very effective as a barrier layer under thermal loading only, and its effectiveness is impaired by tensile strain at the Cu/Ta interface. The simulations also clarified the mechanism that caused the impairment. The methodology and approach described in this paper can be followed further to study the effectiveness of barrier layers under various annealing and strain conditions, and to determine the minimum thickness of barrier layers required for a particular application.

Failure Mechanism of 5 Nm Thick Ta–Si–C Barrier Layers Against Cu Penetration at 750–800°C

5 - Nm -Thick TaSiC Amorphous Films Stable Up to 750°C As a Diffusion Barrier for Copper Metallization

Ultrathin Ru–Ta–C Barriers for Cu Metallization

Thermal stability of Ta-Si-N/Zr barrier in Cu metallization

Low-Resistivity Ru-Ta-C Barriers for Cu Interconnects

Characteristics of Plasma-Treated Amorphous Ta-Si-C Film As a Diffusion Barrier for Copper Metallization

Recent Advances in Barrier Layer of Cu Interconnects

Highly Thermal-Stable Amorphous TaSi2Cx Thin Films

Diffusion Barrier Properties Of Amorphous And Nanocrystalline Ta Films For Cu Interconnects

Thermally stable Mo-Co-B thin film metallic glass as a potential diffusion barrier in Cu/Si contact system

Reliability Studies of Barrier Layers for Cu/PAE Low-K Interconnects.

Study of the sputtered Mo/TaN and Mo-Ta thin film as diffusion barrier for copper metallization

Influence of Tantalum/tantalum Nitride Barriers and Caps on the High-Temperature Properties of Copper Metallization for Wide-Band Gap Applications

Tan/Ta As an Effective Diffusion Barrier for Direct Contact of Copper and Nisi

Effect of Thickness Scaling on the Permeability and Thermal Stability of Ta(N) Diffusion Barrier

High-Temperature Ta Diffusion in the Grain Boundary of Thin Cu Films

A Heating and Diffusion Barrier Based on TaSiNx for Miniaturized IC Devices

Diffusion behavior of Cu/Ta heterogeneous interface under high temperature and high strain: An atomistic investigation

Ultrathin Cusin/P-Sic:H Bilayer Capping Barrier for Cu/Ultralow-K Dielectric Integration

Cu Contact on NiSi/Si with Thin Ru/TaN Barrier

Improvement of Diffusion Barrier Performance of Ru Thin Film by Incorporating a WHfN Underlayer for Cu Metallization