Study on Microstructures and Grain Boundary Penetration Behaviours in Contact Reactive Brazing Joints of 6063 Al Alloy

M. F. Wu,C. Yu,J. Pu

DOI: https://doi.org/10.1179/174328407x236922

IF: 1.8

2008-01-01

Materials Science and Technology

Abstract:Contact reactive brazing on 6063 Al alloy has been conducted by using Cu foil or Cu foil–Mg powder–Cu foil multilayer as interlayer. The microstructures of the joints and grain boundary penetration phenomenon were analysed and discussed primarily. The results showed that the microstructure of the reaction zone consisted of α-Al solid solution and CuAl2 compound as monolayer Cu foil was used, and meantime, obvious grain boundary penetration phenomenon at the reaction interface was found. However, the reaction zone of the joint bonded with Cu foil–Mg powder–Cu foil was composed of Al(Mg, Cu) solid solution, CuAl2 intermetallic compound, Cu–Al–Mg ternary intermetallic compound and Al2MgO4. It was also found that the grain boundary penetration phenomenon was delayed as Mg powder was added into the interlayer.