Abstract:Carbon black powders were incorporated into coarse aluminum and titanium powders, and the mixture was used for a combustion front quenching test. The microstructural evolution in the quenched sample was analyzed with scanning electron microscope (SEM) and energy dispersive spectrometer (EDS). In addition, the combustion temperature and rate were measure, and the phase constituent of the final product was inspected by X-ray diffraction (XRD). The results showed that the combustion reaction started with the melting of the Al particles and formation of Al3Ti around the Ti particles, and it proceeded in a reaction–dissolution–precipitation mechanism. After melting of the Al and formation of Al3Ti, the Ti, especially C particles dissolved into the Al liquid and forming Ti–Al–C solution, as a result, TiC grains precipitated out of the saturated liquid solution. With an increase in temperature, Al3Ti then decomposed and TiC also precipitated from the melt. In the final products, besides TiC particles and Al matrix, a small amount of Al3Ti was also founded. Also, previous results were explained, and a model corresponding to this mechanism was drawn.

Effects of particle size of reactant on characteristics of combustion synthesis of TiC-Fe cermet

Effect of Particle Size of Iron on Reaction Velocity of Combustion Synthesis of Ti-C-Fe System

Dual-solution-precipitation mechanism of combustion synthesis of TiC-Fe cermet with fine Ti powder

Microstructural evolution during combustion synthesis of TiC-Fe cermet

Mechanism of Combustion Synthesis of TiC-Ti Cermet

Role of iron addition in the combustion synthesis of TiC–Fe cermet

Formation of Layer-Shaped Pores in TiC-Fe Cermet by Combustion Synthesis

Microstructural evolution of the titanium particles in the in-situ composition of TiC–Fe by the combustion synthesis

Microstructural evolution during the combustion synthesis of TiC–Al cermet with larger metallic particles

Effect of Fe on the Phases and Microstructure of TiC–Fe Cermets by Combustion Synthesis/quasi-Isostatic Pressing

Effects of TiAl additions on combustion synthesis of Ti3AlC2 powders

Combustion Synthesis of Tinxc1-X Powders with Ultra Fine Particle Size by Using Titanium Oxide As Dilution

Effect of Cu-Ti-C Reaction Composition on Reinforcing Particles Size of TiCx/Cu Composites

Effects of Tic Addition on Combustion Synthesis of Ti(2)Alc Powders

Effects of TiAl3 addition on combustion synthesis of Ti3AlC

Combustion Synthesis of TiC–Fe Composites under the Action of an Electric Field

Soot Combustion Performance and H2-TPR Study on Ceria-Based Mixed Oxides

Effect of Combustion Temperature on Combustion Synthesis of Ti3AlC2 and Ti2AlC

Microstructural Evolution in the Combustion Synthesis of Titanium Carbide

Effects of carbon contents on combustion synthesis of Ti2AlC powders

TiC-Fe cermets fabricated by SHS