Abstract:This study deals with the effect of conventional sintering and microwave sintering on the densification kinetics of Titanium Carbide (TiC) in the presence of Ni (1, 1.5, 2 wt%). TiC compacts were obtained after uniaxial pressing of powders synthesised by ball milling of Titanium and Carbon and sintering was done in the presence of Nickel. The samples prepared were subjected to conventional as well as microwave sintering. The XRD and SEM analysis were used for a study of the reaction of Ti and C powders upon addition of Ni, which reduced the sintering temperature to 1200 °C. The densification of TiC powders was due to the Ti-Ni eutectic system, the liquid phase formed at this temperature assisting the sintering process. The SEM images revealed the flake like structure of TiC in which the carbon diffused into Ti upon the addition of Ni, thereby supporting enhanced mass transfer. The XRD pattern showed the presence of Titanium Oxide (TiO2) along with TiC which resulted in non-uniform distribution of hardness. Maximum hardness was achieved in the conventional sintered compacts which gradually increased with increase in Ni addition. The presence of the oxide phase and the formation of micro cracks resulted in non-uniform hardness for microwave sintered compacts. The maximum hardness of conventional sintered compact (375 HLD) was nearly 1.5 times more than the maximum hardness of the microwave sintered compact (250 HLD). The density of the microwave sintered compact was found to be higher by 8% than with the conventionally sintered compact.

Microstructural Evolution in the Combustion Synthesis of Titanium Carbide

Microstructural evolution of the titanium particles in the in-situ composition of TiC–Fe by the combustion synthesis

Microstructural evolution during combustion synthesis of TiC-Fe cermet

Microstructural evolution during the combustion synthesis of TiC–Al cermet with larger metallic particles

Mechanism of Combustion Synthesis of TiC-Ti Cermet

Structure Formation in the Combustion Synthesis of Al2O3–TiC Composites

Dual-solution-precipitation mechanism of combustion synthesis of TiC-Fe cermet with fine Ti powder

Mechanosynthesis Mechanism of Tic Powders

Microstructure evolution of Fe-Ti-C system synthesized by low temperature combustion induced in electric field

Kinetic Process of Combustion Synthesis of Ternary Carbide Ti<sub>3</sub>AlC<sub>2</sub>

MICROSTRUCTURE OF Si3N4-TiN-SiC CERAMICS DURING COMBUSTION SYNTHESIS PROCESS

Microstructural Evolution During Self-Propagating High Temperature Synthesis of Ti2AlC Machinable Ceramics

Role of iron addition in the combustion synthesis of TiC–Fe cermet

Investigation of TiC formation during ball-milling of elemental titanium and carbon

Formation Mechanism of Spherical TiC in Ni-Ti-C System during Combustion Synthesis

Combustion synthesis of ternary carbide Ti3AlC2 in Ti–Al–C system

Reaction Mechanisms of Combustion Synthesis of Si<sub>3</sub>N<sub>4</sub> -SiC -TiN Ceramics

Microstructure of TiAl/TiC cermet joint bonded by combustion synthesis

Microstructures, Densification and Mechanical Properties of TiC–Al2O3–Al Composite by Field-Activated Combustion Synthesis

Microstructure Transformation and Mechanical Properties of TiC–TiB2 Ceramics Prepared by Combustion Synthesis in High Gravity Field

Microstructure Evolution of Ti-Al-C System Composite