Abstract:Single spinel-phased Zn2Ga3.98-4x/3GexO8:Cr-0.02 (ZGGO:Cr) near infrared (NIR) persistent luminescent nanoparticles (PLNPs) with various Ge4+ concentrations (0.45 <= x <= 0.90) were prepared via an initial hydrothermal synthesis and a subsequent vacuum annealing. Unlike the case of co-substitution of Ge4+ and Zn2+ for Ga3+ via a one-step hydrothermal method, the increase of Ge4+ substitution concentration from 0.45 to 0.90 can lead to the decrease in average particle size from 51.7 to 45.4 nm. Meanwhile, more anti-site Zn'(Ga) -Ga degrees(zn), Ge degrees(Ga) and V-Ga''' . defects are introduced into ZGGO host lattice after Ge4+ substitution and it results in the shallowed trap depths, narrowed band gap and increased NIR afterglow intensity around 700 nm, which derives from the E-2, T-4(2) ->(4)A(2) transitions of surface and interior Cr3+ ions. In our case, not only afterglow imaging but also temperature sensing can be simultaneously realized by constructing a modified ratiometric afterglow nanothermometer based on the temperature-dependent afterglow intensity ratios of T-4(2) -> (4)A(2) to E-2 -> (4)A(2) emissions of surface and interior Cr3+ doped in ZGGO:Cr nanoparticles. Although the decrease in absolute thermal sensitivity from 0.50 to 0.41 K-1 is found at 310 K with increasing Ge4+ substitution concentration from 0.45 to 0.90, the relative thermal sensitivity exhibits an increasing trend, and the maximum relative sensitivity reaches 1.0% K-1 within the physiological temperature window (295-328 K) when x = 0.90. Our results suggest that ZGGO:Cr nanoparticles with an amount of Ge (4+) concentration ranging from 0.75 to 0.90 have potential applications in bioimaging and biosensing. (C) 2020 Elsevier B.V. All rights reserved.

Blue emission of Ge nanocrystals prepared by thermal decomposition

Sol–gel preparation of Ge nanocrystals embedded in SiO2 glasses

Structure and Photoluminescence of Ge Nanoparticles Embedded in SiO2 Gel Glasses Fabricated at Different Temperatures

Photoluminescence of Ge Nanoparticles Embedded in Sio2 Glasses Fabricated by A Sol-Gel Method

Fabrication of Gan Nanodots Via Gan Thermal Decomposition in H-2 Atmosphere

Synthesis of Germanium Nanowires

Photoluminescence from Surface-Oxidized Ge Nanoclusters

Preparation of Ge nanocrystals via ultrasonic solution reduction

Growth Mechanism and Surface Structure of Ge Nanocrystals Prepared by Thermal Annealing of Cosputtered Gesio Ternary Precursor

The Effects of the Amount of Ge4+ Doped in Zn2Ga3.98-4/3Ge O8:Cr0.02 Nanoparticles on Size Distribution, NIR Afterglow Imaging and Temperature Sensing

Nonthermal plasma synthesized freestanding silicon–germanium alloy nanocrystals

PREPARATION OF nc-Ge EMBEDDED IN SiO2 MATRIX AND OBSERVATION OF VISIBLE PHOTOLUMINESCENCE

Solution Synthesis of Germanium Nanocrystals: Success and Open Challenges

Thermal History Effect on the Nucleation of Oxygen Precipitates in Germanium Doped Cz-silicon Studied by High-Energy X-ray Diffraction

Formation Mechanism of Ge Nanocrystals Embedded in SiO2studied by Fluorescence X-Ray Absorption Fine Structure

A New Method for Preparing Ge Nano-Crystallites Embedded in Siny Matrices

Intensive blue light emission from beta-Ga2O3 nanowires, nanotapes and nanosheets by carbothermal synthesis

Single-Crystalline Germanium Nanocrystals via a Two-Step Microwave-Assisted Colloidal Synthesis from GeI4

A Simple Method to Synthesize Β-Ga2o3 Nanorods and Their Photoluminescence Properties

Germanium nanowires: Synthesis, electrical and “catalytic” properties

Germanium Dioxide Nanocubes with Different Size Distributions and Its Gibbs Free Energy Theory