Abstract:β-Ga2O3 nanostructures, including nanowires (NWs), nanosheets (NSHs), and nanorods (NRs), were synthesized using thermally dewetted Au nanoparticles as catalyst in a chemical vapor deposition process. The morphology of the as-grown β-Ga2O3 nanostructures depends strongly on the growth temperature and time. Successful growth of β-Ga2O3 NWs with lengths of 7-25 μm, NSHs, and NRs was achieved. It has been demonstrated that the vapor-liquid-solid mechanism governs the NW growth, and the vapor-solid mechanism occurs in the growth of NSHs and NRs. The X-ray diffraction analysis showed that the as-grown nanostructures were highly pure single-phase β-Ga2O3. The bandgap of the β-Ga2O3 nanostructures was determined to lie in the range of 4.68-4.74 eV. Characteristic Raman peaks were observed with a small blue and red shift, both of 1-3 cm-1, as compared with those from the bulk, indicating the presence of internal strain and defects in the as-grown β-Ga2O3 nanostructures. Strong photoluminescence emission in the UV-blue spectral region was obtained in the β-Ga2O3 nanostructures, regardless of their morphology. The UV (374-377 nm) emission is due to the intrinsic radiative recombination of self-trapped excitons present at the band edge. The strong blue (404-490 nm) emissions, consisting of five bands, are attributed to the presence of the complex defect states in the donor (VO) and acceptor (VGa or VGa-O). These β-Ga2O3 nanostructures are expected to have potential applications in optoelectronic devices such as tunable UV-Vis photodetectors.

A Simple Method to Synthesize Β-Ga2o3 Nanorods and Their Photoluminescence Properties

Gallium oxide nanorods by the conversion of gallium oxide hydroxide nanorods

Synthesis and photoluminescence of gallium oxide ultra-long nanowires and thin nanosheets

Microwave-assisted Synthesis of Various Gallium Oxyhydroxide Nanorods and Their Controllable Conversion into Different Gallium Oxide Polymorphs

The synthesis, structure and cathodoluminescence of ellipsoid-shaped ZnGa<sub>2</sub>O<sub>4</sub>nanorods

Large-scale Synthesis of GaN Nanorods and Their Photoluminescence

Synthesis of High Crystallization Β-Ga2o3 Micron Rods with Tunable Morphologies and Intensive Blue Emission Via Solution Route

Microwave Hydrothermal Synthesis of Gan Nanorods

Synthesis of ZnGa2O4 nanowires with β-Ga2O3 templates and its photoluminescence performance

The Synthesis, Structure And Cathodoluminescence Of Ellipsoid-Shaped Znga2o4 Nanorods

Controllable Chemical Reaction Synthesis of Tb(OH)3 Nanorods and Their Photoluminescence Property

A simple method to synthesize gallium oxide nanosheets and nanobelts

Synthesis of Ultrafine Lanthanum Hydroxide Nanorods by A Simple Hydrothermal Process

Synthesis and characterization of gallium oxide nanowires via a hydrothermal method

Synthesis, Raman Scattering And Defects Of Beta-Ga2o3 Nanorods

β-Ga2O3 Nanostructures: Chemical Vapor Deposition Growth Using Thermally Dewetted Au Nanoparticles as Catalyst and Characterization

High-Aspect Ratio β-Ga2O3 Nanorods via Hydrothermal Synthesis

Study of GaN Nanorods Converted from Β-Ga2o3

Ultraviolet photoluminescence of β-Ga2O3 microparticles synthesized by hydrothermal method

Soft-Template mediated synthesis of GaOOH nanorod-shelled microspheres and thermal conversion to β-Ga 2O 3

Facile Synthesis and Characterization of Β-Ga[sub 2]o[sub 3] Nanostructures Via Vapor Transport Method