Abstract:Dy(3+)-doped gallium oxide hydroxides (GaOOH:Dy(3+)) with various morphologies (submicrospindles, submicroellipsoids, 3D hierarchical microspheres) were synthesized by a facile soft-chemical method. After annealing at 1000 degrees C, the GaOOH:Dy(3+) precursor was easily converted to beta-Ga(2)O(3):Dy(3+) phosphors which kept their original morphologies. The as-prepared GaOOH:Dy(3+) and beta-Ga(2)O(3):Dy(3+) products were characterized using X-ray diffraction (XRD), field-emission scanning electron microscopy (FESEM), low- to high-resolution transmission electron microscopy (TEM), selected area electron diffraction (SAED), photoluminescence (PL) spectra, cathodoluminescence (CL) spectra, and quantum yield (QY). With an increase in pH from 4 to 9, the morphology of GaOOH:Dy(3+) varied from submicrospindles to 3D hierarchical microspheres of self-assembled nanoparticles. A possible mechanism for the formation of various morphologies of GaOOH:Dy(3+) and beta-Ga(2)O(3):Dy(3+) was proposed. Under ultraviolet and low-voltage electron beam excitation, the pure beta-Ga(2)O(3) samples exhibit a blue emission with a maximum at 438 nm originating from the GaO(6) groups, while the beta-Ga(2)O(3):Dy(3+) samples show the characteristic emission of Dy(3+) corresponding to (4)F(9/2) --> (6)H(15/2, 13/2) transitions due to an efficient energy transfer from beta-Ga(2)O(3) to Dy(3+). A simple model was proposed to explain the energy transfer process and luminescence mechanism. Furthermore, the dependence of luminescence intensity on the morphology has been investigated in detail. Under 257 nm UV and electron beam excitation, the beta-Ga(2)O(3):Dy(3+) phosphor with a submicroellipsoid shape shows the highest relative emission intensity and quantum yield compared with other morphologies, and the obtained phosphors have potential applications in the areas of fluorescent lamps and field emission displays (FEDs).

Synthesis of High Crystallization Β-Ga2o3 Micron Rods with Tunable Morphologies and Intensive Blue Emission Via Solution Route

A Simple Method to Synthesize Β-Ga2o3 Nanorods and Their Photoluminescence Properties

Intensive blue light emission from beta-Ga2O3 nanowires, nanotapes and nanosheets by carbothermal synthesis

Gallium oxide nanorods by the conversion of gallium oxide hydroxide nanorods

Microwave-assisted Synthesis of Various Gallium Oxyhydroxide Nanorods and Their Controllable Conversion into Different Gallium Oxide Polymorphs

Fabrication and Characterization of Β-Ga2o3 Optical Nanowires

Catalyst-free Growth of Β-Ga2o3 Microstructures by Thermal Oxidation

Characteristics of 4-Inch (100) Oriented Mg-doped Β-Ga2o3 Bulk Single Crystals Grown by a Casting Method

Study of β-Ga2O3 Ceramics Synthesized under Powerful Electron Beam

Facile Synthesis And Characterization Of Gallium Oxide (Beta-Ga2o3) 1d Nanostructures: Nanowires, Nanoribbons, And Nanosheets

A simple method to synthesize gallium oxide nanosheets and nanobelts

Shape-Controllable Synthesis and Morphology-Dependent Luminescence Properties of Gaooh:Dy3+ and Beta-Ga2o3:Dy3+

Facile synthesis of β-Ga2O3 based high-performance electronic devices via direct oxidation of solution-processed transition metal dichalcogenides

Synthesis of 1d and Heavily Doped Zn1-Xcoxo Six-Prism Nanorods: Improvement of Blue-Green Emission and Room Temperature Ferromagnetism

Facile Synthesis and Characterization of Β-Ga[sub 2]o[sub 3] Nanostructures Via Vapor Transport Method

Microwave Hydrothermal Synthesis of Gan Nanorods

β-Ga2O3 Nanostructures: Chemical Vapor Deposition Growth Using Thermally Dewetted Au Nanoparticles as Catalyst and Characterization

Growth and Photocatalytic Properties of Gallium Oxide Films Using Chemical Bath Deposition

Advanced Fabrication of 3D Micro/Nanostructures of Gallium Oxide with a Tuned Band Gap and Optical Properties

Synthesis and characterization of ultrathin single-crystalline cerium oxide nanorods

Direct Synthesis of Gallium Oxide Tubes, Nanowires, and Nanopaintbrushes