Abstract:The distribution of copper and lead between copper rich alloy and alumina saturated flash smelting slag produced from Polish copper concentrates was investigated at 1673 and 1553 K under controlled oxygen partial pressures in the range from 8.6·10−13 to 3.1·10−7 atm in order to obtain fundamental information related to single stage flash smelting of Polish copper concentrates and decopperizing of the flash smelting slags. The slope of the linear relationship between the logarithmic distribution ratio and oxygen partial pressure shows that the predominant species dissolved in the slag are CuO0.5 and Cu for copper and PbO and Pb for lead. Activity coefficients for all these copper and lead species in the slag were determined and compared with those in synthetic SiO2-CaO-Al2O3-FeOx and SiO2-CaO-Al2O3-MgO-FeOx slags containing up to 7.5 mass% iron. Existence of a miscibility gap in the flash smelting slag was confirmed at the oxygen partial pressures used in the experiments. The results were used to explain the thermodynamic reasons behind potential problems in the decopperizing of the flash smelting slag. On a investigué la distribution du cuivre et du plomb entre un alliage riche en cuivre et la scorie de la fusion éclair saturée en oxyde d’aluminium, produite à partir de concentrés de cuivre polonais, à 1673 et 1553 K, sous des pressions partielles contrôlées d’oxygène dans la gamme de 8.6·10−13 à 3.1·10−7 atm. L’objectif était d’obtenir l’information fondamentale reliée à la fusion éclair à étape unique des concentrés de cuivre polonais et au décuivrage des scories de la fusion éclair. La pente de la relation linéaire entre le ratio de distribution logarithmique et la pression partielle de l’oxygène montre que les espèces prédominantes dissoutes dans la scorie sont le CuO0.5 et le Cu pour le cuivre et le PbO et le Pb pour le plomb. On a déterminé les coefficients d’activité de toutes ces espèces de cuivre et de plomb dans la scorie et on les a comparés avec ceux de scories synthétiques SiO2-CaO-Al2O3-FeOx et SiO2-CaO-Al2O3-MgO-FeOx contenant jusqu’à 7.5% en masse de fer. On a confirmé l’existence d’une interruption de miscibilité dans la scorie de la fusion éclair aux pressions partielles d’oxygène utilisées dans les expériences. On a utilisé les résultats pour expliquer les raisons thermodynamiques derrière les problèmes potentiels de décuivrage de la scorie de la fusion éclair.

Studies on the Behavior of Copper in the Process of Pressure Alkali Treating Lead Copper Matte

P-type Transparent Conducting Copper Aluminum Oxide Films with Different Cu/Al Ratio

THERMODYNAMICS OF COPPER AND LEAD IN ALUMINA SATURATED FLASH SMELTING SLAG

Experimental Study on the Phase Equilibrium of Copper Matte and Silica-Saturated FeO X -Sio 2 -Based Slags in Pyrometallurgical WEEE Processing

Equilibrium of Copper Matte and Silica-Saturated Iron Silicate Slags at 1300 °C and PSO2\documentclass[12pt]{minimal} \usepackage{amsmath} \usepackage{wasysym} \usepackage{amsfonts} \usepackage{amssymb} \usepackage{amsbsy} \usepackage{mathrsfs} \usepackage{upgreek} \Setlength{\oddsidemargin}{-69Pt}

Influence of impurities on the sintering densification in nano- Al2O3 powders coated by copper

Equilibrium of Copper Matte and Silica-Saturated Iron Silicate Slags at 1300 °C and $$ P_{{{\text{SO}}_{ 2} }} $$ of 0.5 Atm

Electroless Plating of Copper on Al2o3 and Its Heat Treatment Behaviour

Multiphase Equilibrium Relationships between Copper Matte and CaO-Al2O3-Bearing Iron Silicate Slags in Combined Smelting of WEEE and Copper Concentrates

Thermodynamics analysis for Ag/CuO composites by reactive synthesis

Chemical Processes of the Formation of Copper(I) Oxide on Copper Foil under Hydrothermal Conditions

Investigation of the post-treatment process for improving corrosion behaviors and adhesion strength of plasma electrolytic oxidation (PEO) coatings on pure copper

Mechanism of Protective Cover and Melting Loss of Copper Melt

Thermodynamic Properties And Transport Coefficients Of Co2-Cu Thermal Plasmas

Thermodynamic Phase Conversion Mechanism on Copper–Cobalt Slag Cleaning Process Using Gypsum Wastes as Sulfurizing Agent

Thermodynamics Evaluation and Verification of High-Sulfur Copper Slag Composite Agglomerate in Oxidation-Roasting-Separation-Leaching Process

Preparation and Stability Research of Cuprous Oxide by Electrolytic Process

Controlled Corrosion Behaviors of Copper in Oxidizer Solutions for Chemical Mechanical Polishing: Influence of the Decomposition Products

Development and application of matte/speiss/metal thermodynamic database for optimization of processing of drosses, dusts and reverts from lead, zinc and copper production

STUDY ON THE THERMODYNAMICS OF CuO／Al IN SITU Al2O3 REINFORCED Al MATRIX COMPOSITES

Investigation of atmospheric pressure leaching conditions and leaching kinetics in the obtaining of industrial copper (II) acetate solution from copper slags