Abstract:The synthesis of SnO 2 nanoparticles doped with varying concentrations of Fe was carried out using the sol–gel method. The resulting samples underwent analysis using X-ray diffraction (XRD), high-resolution transmission electron microscopy (HR-TEM), ultraviolet–visible spectroscopy (UV–Vis), diffuse reflectance spectroscopy (DRS), photoluminescence spectroscopy, and vibrating sample magnetometry. The purpose of this investigation was to examine the impact of doping on the structural, optical, and magnetic properties of the nanoparticles. The XRD study demonstrated a discernible alteration in the size of the crystalline structure as a function of the concentration of doping. The study revealed a noticeable variation in crystallite size, ranging from ~ 13 to 5 nm, as the Fe doping concentration increased from 0 to 7 mol%. This observation suggested that the rise in Fe content effectively hindered crystal development. The estimation of the optical band gap was performed using the Kubelka–Munk equation, revealing a decrease in the band gap for a specific doping concentration of Fe. The photoluminescence (PL) spectra obtained at room temperature indicated a red shift in the peak positions of the pristine SnO 2 samples upon Fe doping. This observation provides confirmation of the reduction in the band gap of SnO 2 resulting from the incorporation of Fe dopants. The nanoparticles doped with 5% Fe exhibited superior optical characteristics compared to the remaining samples. Furthermore, magnetic properties were determined by investigating magnetization vs. applied fields. Ferromagnetic interaction was observed in all the systems of SnO 2 doped with Fe. To achieve a comprehensive understanding, the utilization of density functional theory was employed. The electronic states and density of states behavior were computed to accurately anticipate the arrangement of lattice sites and the corresponding presence of atoms. Theoretical computations were conducted using the VASP program.

Synthesis and Magnetic Properties of SnFe2O4 Nanoparticles

Synthesis of Nanocrystalline Ferrites Zn0.4ni0.6cr0.5laxfe1.5-Xo4 and Its Magnetic Properties

Zn-Cu-codoped SnO2 Nanoparticles: Structural, Optical, and Ferromagnetic Behaviors

Zn-doped SnO2 Nanoparticles: Structural, Optical, Dielectric and Magnetic Properties

Synthesis and Magnetic Properties of Pt3Co/Fe3O4Nanocomposites

Synthesis of CoFe2O4 Nanoparticles via Solution Method and Their Magnetic Properties

Structure And Magnetic Properties Of Co2.73fe0.27o4 Synthesized By The Heat-Decomposition Method

ZnFe2O4 Nanocrystals: Synthesis and Magnetic Properties

Mössbauer and magnetic studies of Fe-doped ZnO nanoparticles prepared by solution co-precipitation method

Synthesis of Fe3O4 Nanoparticles and Their Magnetic Properties

Synergistic Insights into the Structural, Optical, and Magnetic Features of Iron-Modified Tin Oxide (Fe-SnO2) Nanoparticles: An Integrated Experimental and First Principles Investigation

High-temperature Solid State Synthesis and Characterization in Magnetic and Transporting Properties of Zn_xFe_(3-x)O_4 Powder

Synthesis of Fe$_3$O$_4$ nanoparticles and their magnetic properties

High Temperature Stable Monodisperse Superparamagnetic Core-Shell Iron-Oxide@Sno2 Nanoparticles

Preparation and Magnetic Properties of Fe3+–Nb5+ Co-Doped SnO2

Synthesis of SnFe2O4 Nanomaterials Via High Energy Ball Milling of SnO (Stannous) and α-Fe2O3 (Hematite) Solid Precursors

Synthesis of Sn(1-X)Fex@Feysn(1-Y)Oz Nanohybrids Via A Simple Programmed Microfluidic Process

Characterization and magnetic properties of CoFe2O4 nanoparticles synthesized by the co‐precipitation method

Chemical synthesis and magnetic properties of monodisperse cobalt ferrite nanoparticles

A Simple Solution Route to Control Synthesis of Fe3O4 Nanomaterials at Low Temperature and Their Magnetic Properties

Synthesis and Magnetic Properties of Mn-Zn Ferrite Nanoparticles