Abstract:We report a novel approach to enhance thermal stability of magnetite nanoparticles by entrapping them in silver matrix. The oleic acid capped nanoparticles of average crystallite size ˜10 nm were synthesized through co-precipitation, followed by hydrothermal microwave assisted capping of magnetite nanoparticles with Ag matrix in ethylene glycol solvent. At ˜160 °C the oleic acid is desorbed from the magnetite nanoparticles, and silver is deposited on negatively charged magnetite seeds through electrostatic attraction. The prepared particles are characterized by X-ray diffraction, high resolution transmission electron microscopy, dynamic light scattering and UV-vis spectroscopy. The surface plasmon resonance band at 479 nm and large average hydrodynamic diameter of ˜432 nm confirm the Ag matrix around the magnetite particles. Thermal stability of prepared particles was assessed using in situ high temperature XRD, thermo gravimetric analysis and differential scanning calorimetry and the results are compared with that of oleic acid capped particles. Magnetite nanoparticles in silver matrix showed no phase conversion up to 900 °C, while oleic acid capped and bare nanoparticles are phase converted to nonmagnetic α-Fe₂O₃ phase between 400-450 °C, under vacuum annealing. A rapid growth of Fe₃O₄ nanoparticles at higher temperature was observed due to faster coalescence through diffusion and higher surface free energy of magnetite as compared to silver. The saturation magnetization of oleic acid capped magnetite particles in silver matrix before and after vacuum annealing at 900 °C were 25.4 and 46.7 emu/g, respectively. The retention of superparamagnetic behavior in silver matrix up to 900 °C is interesting for high temperature applications.

High Temperature Stable Monodisperse Superparamagnetic Core-Shell Iron-Oxide@Sno2 Nanoparticles

Low-Temperature Synthesis of Superparamagnetic Nanocomposite Particles Composed of Platinum and Maghemite

Size-controlled synthesis of monodisperse superparamagnetic iron oxide nanoparticles

Solvothermal Synthesis and Magnetic Property of Monodispersed Fe_3O_4 Nano-powders

Polyol Synthesis of Superparamagnetic Fe_3O_4 Nanoparticles for Magnetic Resonance Imaging

A Novel Approach to Enhance High Temperature Thermal Stability of Superparamagnetic Fe₃O₄ Nanoparticles

Magnetite Fe3O4 Nanoparticles and Hematite Α-Fe2o3 Uniform Oblique Hexagonal Microdisks, Drum-Like Particles and Spindles and Their Magnetic Properties

Stabilized Bare Superparamagnetic Iron Oxide Nanoparticles: Synthesis and Characterization

Synthesis of CoFe2O4 Nanoparticles via Solution Method and Their Magnetic Properties

Preparation of Superparamagnetic Cobalt Ferrite Nanoparticles with High Saturation Magnetization by Temperature-Controlled Co-Precipitation Method

Controlled Synthesis of Cobalt-Doped Magnetic Iron Oxide Nanoparticles

Synthesis and characterization of core-shell structure silica-coated Fe29.5Ni70.5 nanoparticles

Controlled synthesis and anomalous magnetic properties of relatively monodisperse CoO nanocrystals.

Synthesis of Fe-group Metal Oxide Nanostructures by Thermal Oxidation and Their Magnetic Properties.

Ultrafast Preparation Of Monodisperse Fe3o4 Nanoparticles By Microwave-Assisted Thermal Decomposition

Synthesis, Surface Modification and Magnetic Properties Analysis of Heat-Generating Cobalt-Substituted Magnetite Nanoparticles

Synthesis of N-Hexadecylphosphonic Acid-Coated Monodisperse Fe3O4 Superparamagnetic Nanoparticles

Highly Stable Alumina-Coated Iron Nanocomposites Synthesized by Wet Chemistry Method

Self-propagating High Temperature Synthesis of Ni<SUB>0.35</SUB>Zn<SUB>0.65</SUB>Fe<SUB>2</SUB>O<SUB>4</SUB> using Various Ni-containing Species

Synthesis of Nanometer-Size Maghemite Particles from Magnetite

A Simple Solution Route to Control Synthesis of Fe3O4 Nanomaterials at Low Temperature and Their Magnetic Properties