Ambient Catalytic Spinning of Polyethylene Nanofibers
Ruikai Wu,Tim M. Lenz,Fayez Abdullah S Alfayez,Ruohan Zhao,Patrick rupper,Edith Perret,Sandro Lehner,Milijana Jovic,Sabyasachi Gaan,Bernhard Rieger,Manfred Heuberger
DOI: https://doi.org/10.1002/anie.202315326
2024-01-18
Angewandte Chemie International Edition
Abstract:A novel single-atom Ni(II) catalyst (Ni-OH) is covalently immobilized onto the nano-channels of mesoporous Santa Barbara Amorphous (SBA)-15 particles and isotropic Anodized Aluminum Oxide (AAO) membrane for confined-space ethylene extrusion polymerization. The presence of surface-tethered Ni complexes (Ni@SBA-15 and Ni@AAO) is confirmed by the inductively coupled plasma-optical emission spectrometry (ICP-OES) and X-ray photoelectron spectroscopy (XPS). In the catalytic spinning process, the produced PE materials exhibit very homogeneous fibrous morphology at nanoscale (diameter: ~50 nm). The synthesized PE nanofibers extrude in a highly oriented manner from the nano-reactors at ambient temperature. Remarkably high Mw (1.62 × 106 g mol−1), melting point (124 °C), and crystallinity (41.8%) are observed among PE samples thanks to the confined-space polymerization. The chain-walking behavior of surface tethered Ni catalysts is greatly limited by the confinement inside the nano-channels, leading to the formation of very low-branched PE materials (13.6/1000C). Due to fixed supported catalytic topology and room temperature, the filaments are expected to be free of entanglement. This work signifies an important step towards the realization of a continuous mild catalytic-spinning (CATSPIN) process, where the polymer is directly synthesized into fiber shape at negligible chain branching and elegantly avoiding common limitations like thermal degradation or molecular entanglement.
chemistry, multidisciplinary