Abstract:The effect of coating cracking during depth-sensing indentation testing (e.g. nanoindentation testing) on systems comprising thin hard coatings (e.g. TiN) on a less stiff, hard substrate (e.g. steel) has been investigated in order to establish whether, at such small scales, the occurrence of annular through-thickness cracks around indentation sites can be detected from load–displacement plots and whether any accompanying localized debonding of the coating from the substrate can also be identified. Experiments were performed on thin TiN and NbN monolayers, and compositionally modulated TiN/NbN and TiN/ZrN deposited onto hard steel or stainless steel substrates. Above a critical load (Pcrit) in the range 80–500mN, all systems exhibited annular through-thickness cracks around indentation sites. The cracking was found to be accompanied by a discrete change in gradient of the loading portion of the load–displacement curve. Also, analysis of the unloading curves beyond this point showed that elastic recovery was controlled by the elastic modulus of the underlying substrate material alone. The cracking mechanism has been characterized using scanning electron microscopy, coupled with optical profilometry to map the detailed z-displacement of the surface — a procedure critical to understanding whether coating–substrate debonding had occurred. Some cracks were found to show a spiral morphology and the effect of indentation loading rate was investigated to see if appearance of these cracks was loading-rate sensitive. Our results highlight the problems inherent in assessing both the interfacial failure and the interfacial fracture toughness of thin film coated systems at the small contact scales (⩽1μm) associated with crack genesis where it is difficult to confirm the extent of sub-surface cracks by conventional means. We have also demonstrated that both load–displacement and load–displacement squared plots are necessary if a more complete understanding of system behaviour is to be gained. Also, a simple fracture mechanics model for the annular cracking behaviour seen in such systems has been derived and used to estimate a value of Gic (the interfacial work of fracture) as 180Jm−2 for the TiN/ZrN-stainless steel system.

Fracture from Knoop Indentation-Induced Flaws in Sintered Silicon Carbide and Hot-Pressed Silicon Nitride

Strength/Crack-Size Relationship for Knoop-Indented Bending Specimens and Its Application to Silicon Nitride Ceramics

Fracture Toughness Evaluation and Plastic Behavior Law of a Single Crystal Silicon Carbide by Nanoindentation

Variation in the indentation toughness of silicon nitride

R-curve Behavior of Indentation Cracks in Silicon Nitride Based Ceramic Composite

Statistical properties of indentation toughness for silicon nitride ceramic

Micromechanical characterization of zirconia and silicon nitride ceramics using indentation and scratch methods

Mechanism of crack evolution in nano-indentation of single crystal silicon by atomistic simulations and theoretical analysis

Evaluation by Indentation of Fracture Toughness of Ceramic Materials

Crack-Location-Dependent R-Curve Behavior in Si3n4

Assessing fracture toughness in sintered Al2O3–ZrO2(3Y)–SiC ceramic composites through indentation technique

On understanding the mechanical properties and damage behavior of C f /SiC composites by indentation method

A coupled approach to predict cone-cracks in spherical indentation tests with smooth or rough indenters

Transformation Driving Force for Indentation Cracking in Zirconia Ceramics

Nanoindentation stress-strain for Fracture Analysis and computational modeling for hardness and modulus

Depth-sensing ductile and brittle deformation in 3C-SiC under Berkovich nanoindentation

Indentation deformation and microcracking in β-Si 3N 4-based nanoceramic

The effect of coating cracking on the indentation response of thin hard-coated systems

Effects of infilling materials on mechanical behaviors and cracking process of pre-cracked rock: Insights from a hybrid continuum-discontinuum method

Indentation of Coatings at micro/nano scale: Crack formation and deflection

In situ observation of fracture in homogeneous and functionally graded 6061Al/SiCp composites