Abstract:OBJECTIVES: Fractographic analysis of indentation cracks is performed following flexure testing as part of the ASTM (1999) standard for fracture toughness, KIc, determination in advanced ceramics. This method depends on the conduciveness of the material towards fractographic interpretation. The purpose of this study was to evaluate the use of fractography in fracture toughness methods with a feldspathic dental porcelain, in which KIc was measured fractographically as well as numerically using two controlled-flaw beam bending techniques.METHODS: The following methods for KIc determination were applied to a dental porcelain containing a leucite volume fraction of 15-20%: (1) surface crack in flexure (SCF) (dependent upon fractographic analysis); and (2) indentation strength (IS) at indentation loads of 9.8 and 19.6 N (applying both standard numeric calculations and fractographic analysis). The testing environments were (1) ambient air (IS and SCF) and (2) flowing dry nitrogen (SCF).RESULTS: No significant differences were found between numeric and fractographic KIc values for the IS technique at both indentation loads (9.8 and 19.6 N) in ambient air, although KIc values were sensitive to indentation load. Due to the presence of residual stresses, stable crack extension was observed fractographically in all IS specimens, as evidenced by differences between initial (ainitial) and critical (acritical) crack dimensions. For the SCF method, there was a significant difference in toughness between specimens tested in air versus dry nitrogen, however no fractographic evidence for chemically assisted slow crack growth (SCG) was observed.SIGNIFICANCE: The SCF method as described by the ASTM standard was applicable to the feldspathic porcelain and produced very comparable results with the numeric toughness calculations of the IS procedure. However, fractographic analysis of the surface crack was somewhat difficult for this glassy ceramic compared with polycrystalline ceramics. Knowledge about stable crack extension or slow crack growth and its fractographic appearance is essential when estimating the toughness from examination of flaw dimensions on fractured surfaces since large calculation errors may occur if these effects are not taken into account.

Evaluation by Indentation of Fracture Toughness of Ceramic Materials

Indentation toughness of ceramics: a statistical analysis

Fracture toughness (KIc) of a dental porcelain determined by fractographic analysis

Fracture toughness (Kic) of cemented carbides

Fracture Toughness of Advanced Structural Ceramics: Applying ASTM C1421

Statistical properties of indentation toughness of ceramics

Fracture Toughness Evaluation and Plastic Behavior Law of a Single Crystal Silicon Carbide by Nanoindentation

Fracture from Knoop Indentation-Induced Flaws in Sintered Silicon Carbide and Hot-Pressed Silicon Nitride

Indentation toughness of ceramics: A modified approach

A New Approach to Evaluate Fracture Toughness of Structural Materials

Evaluation of the Fracture Toughness KIc for Selected Magnetron Sputtering Coatings by Using the Laugier Model

Micromechanical characterization of zirconia and silicon nitride ceramics using indentation and scratch methods

Fracture behavior of lithia disilicate- and leucite-based ceramics

Determination of K ISCC by indentation in ceramics

Transformation Driving Force for Indentation Cracking in Zirconia Ceramics

Statistical properties of indentation toughness for silicon nitride ceramic

Fracture resistance of Ceramic-Polymer hybrid materials using microscopic finite element analysis and experimental validation

Assessing fracture toughness in sintered Al2O3–ZrO2(3Y)–SiC ceramic composites through indentation technique

Evaluations on Ceramic Fracture Toughness Measurement by Edge Chipping

A Fracture toughness criterion for concrete

A Practical Interpolation Method for Determining Cohesion Toughness K_(Ic)~c of Double-K Fracture Model