Abstract:Bulk glassy alloy rods with a diameter of 20mm were produced for Zr61Ti2Nb2Al7.5Ni10Cu17.5 and Zr60Ti2Nb2Al7.5Ni10Cu18.5 by a tilt casting method. The replacement of Zr by a small amount of Ti and Nb caused a distinct increase in the maximum diameter from 16 mm for Zr65Al7.5Ni10Cu17.5 to 20 mm, accompanying the decrease in liquidus temperature and the increase in reduced glass transition temperature. The primary precipitation phase from supercooled liquid also shows a distinct change, i.e., from coexistent Zr2Cu,Zr2Ni and Zr6NiAl2 phases for the 65%Zr alloy to an icosahedral phase for the 61%Zr and 60%Zr alloys. These results allow us to presume that the enhancement of the glass-forming ability is due to an increase in the stability of supercooled liquid against crystallization caused by the development of icosahedral short-range ordered atomic configurations. The 60%Zr specimens taken from the central and near-surface regions in the transverse cross section at the site which is 15 mm away from the bottom surface of the cast glassy rod with a diameter of 20 turn exhibit good mechanical properties under a compressive deformation mode, i.e., Young's modulus of 81 GPa, large elastic strain of 0.02, high yield strength of 1610 MPa and distinct plastic strain of 0.012. Besides, a number of shear bands are observed along the maximum shear stress plane on the peripheral surface near the final fracture site. The finding of producing the large scale Zr-based bulk glassy alloys exhibiting reliable mechanical properties is encouraging for future advancement of bulk glassy alloys as a new type of functional material. [doi: 10.2320/matertrans.MER2008179]

Phase Transformation and Mechanical Properties of Zr-base Bulk Glass-Forming Alloys

Formation, Thermal Stability and Mechanical Properties of Bulk Glassy Alloys with a Diameter of 20 Mm in Zr-(Ti,Nb)-Al-Ni-Cu System

Formation and Phase Evolution of Liquid Phase-Separated Metallic Glasses with Double Glass Transition, Crystallization and Melting

Thermophysical and Mechanical Properties of Multicomponent Zr37Hf16Ni12.5Cu12.5Al1 1co6nb5 Bulk Glass-Forming Alloy

Formation of Zr70Ni23Ti7 Glassy Alloy and Phase Transformation Upon Annealing

Thermophysical and Mechanical Properties of Multicomponent Zr37Hf16Ni12.5Cu12.5Al11Co6Nb5 Bulk Glass-Forming Alloy

Quasicrystallization of (zr<sub>65</sub>al<sub>7.5</sub>cu<sub>27.5</sub>)<sub>95</sub>ti<sub>5</sub> Glassy Alloy

Metastable Phase Separation and Duplex Metallic Glass Formation of Liquid Zr35Al23Ni22Gd20 Alloy

Amorphous-to-quasicrystalline transformation in Zr65Ni10Cu7.5Al7.5Ag10 bulk metallic glass

Quasicrystallization of (Zr<sub>65</sub>Al<sub>7.5</sub>Cu<sub>27.5</sub>)<sub>95</sub>Ti<sub>5</sub> Glassy Alloy

Bulk Amorphous, Nano-Crystalline and Nano-Quasicrystalline Alloys. IV. Thermal Stability and Mechanical Strength of Bulk Glassy Ni-Nb-Ti-Zr Alloys.

Bulk Glassy and Quasicrystalline (Zr65Al7.5Cu27.5)100−xTix Alloys and Their Mechanical Properties

Phases in the Crystallization Process of Zr65al7.5ni10cu17.5 Metallic Glass

Synthesis and Thermal Stability of New Ni-Based Bulk Glassy Alloy with Excellent Mechanical Properties

Thermal Stability and Mechanical Properties of Bulk Glassy Cu-Zr-Ti-(Nb, Ta) Alloys

Metastable Phases, Quasicrystals and Solid Solutions in Zr-Based Bulk Glass-Forming Alloys

Formation and Mechanical Properties of Bulk Glassy and Quasicrystalline Alloys in Zr-Al-Cu-Ti System

Thermal Stability and Mechanical Properties of Zr50Ti5Cu18Ni17Al10 Bulk Metallic Glass

Structure and properties of Zr–Ta–Cu–Ni–Al bulk metallic glasses and metallic glass matrix composites

Bulk Glassy and Quasicrystalline (Zr<SUB>65</SUB>Al<SUB>7.5</SUB>Cu<SUB>27.5</SUB>)<SUB>100&minus;<I>x</I></SUB>Ti<I><SUB>x</SUB></I> Alloys and Their Mechanical Properties

Superplastic deformation behavior of Zr41.25Ti13.75Ni10Cu12.5Be22.5 bulk metallic glass in the supercooled liquid region