Abstract:Based on gradient control of carbon partitioning between martensite and austenite during heat treatment of steels, a stepping-quenching-partitioning (S-Q-P) process is developed for high strength steels. The S-Q-P process involves several quenching processes at progressively lower temperatures between martensite-start ( M s ) and martensite-finish ( M f ) temperatures, each followed by a partitioning treatment at either the initial quenching temperature or above that temperature. A novel microstructure is designed based on the S-Q-P process. Sizes and distributions of retained austenite and high-carbon martensite surrounded by martensite laths can be manipulated by the partitioning duration and temperature, and quenching temperature of the S-Q-P process. Alloying element Si is employed in the S-Q-P steel to suppress formation of carbides and create suitable amount of retained austenite. A steel of 0.39C-1.22Mn-1.12Si-0.23Cr (wt.%) treated by the S-Q-P process is endowed with some special microstructural characteristics: some strips of retained austenite located at edges of martensite blocks with high density of dislocations and between martensite laths, some small blocks of twinned martensites distributed among bundles of the low-carbon martensite lath. The mechanical properties of the medium carbon steel after the S-Q-P process can reach ultimate tensile strength ( Rm ) of 1240 MPa, total elongation ( EI ) of 25%, and product of strength and ductility ( PSD ) of 31.2 GPa% that are much more improved than those after the conventional quenching-tempering (Q-T) and currently prevailing quenching-partitioning (Q-P) treatments. The PSD of the tested steel after the S-Q-P process increases by 67% and 32% as compared with those after the Q-T and Q-P processes, respectively.

Characterization of Microstructure and Mechanical Properties of a Nb-Microalloyed Steel after Quenching-Partitioning-Tempering Process

Microstructural and Mechanical Properties Development During Quenching-Partitioning-Tempering Process of Nb-V-Ti Microalloyed Ultra-High Strength Steel

A novel microstructural design and heat treatment technique based on gradient control of carbon partitioning between austenite and martensite for high strength steels

A Carbide-Free Bainite/martensite/austenite Triplex Steel with Enhanced Mechanical Properties Treated by a Novel Quenching–partitioning–tempering Process

Study of Quenching and Partitioning (Q&P) and Ultrasonic Surface Rolling (USR) Process on Microstructure and Mechanical Property of a High-Strength Martensitic Steel

Mechanical Properties of Steels Treated by Q-P-T Process Incorporating Carbide-free-bainite/martenite Mutiphase Microstructure

Microstructural Evolution of a Low-Carbon Steel during Application of Quenching and Partitioning Heat Treatments after Partial Austenitization

Effect of Deformation on Microstructure and Mechanical Properties of Medium Carbon Steel During Heat Treatment Process

Structure–mechanical Property Relationship in a Low Carbon Nb–Cu Microalloyed Steel Processed Through a Three-Step Heat Treatment: the Effect of Tempering Process

The Fabrication of Ultrahigh-Strength Steel with a Nanolath Structure via Quenching-Partitioning-Tempering

Stepping-quenching-partitioning Treatment of 20simn2mova Steel and Effects of Carbon and Carbide Forming Elements

Effect of tempering and partitioning (T&P) treatment on microstructure and mechanical properties of a low-carbon low-alloy quenched and dynamically partitioned (Q-DP) steel

Tailoring the Microstructure using Quenching and Partitioning Processing in a Commercial Mn-Si-Cr Spring Steel to Improve Tensile Properties

Microstructure Transformation on Pre-Quenched and Ultrafast-Tempered High-Strength Multiphase Steels

Revealing carbide precipitation effects and their mechanisms during quenching-partitioning-tempering of a high carbon steel: Experiments and Modeling

Microstructure Features and Tensile Properties of a Recent Ultra-High-Strength Steel via Two-Step Quenching and Partitioning Process

The Microstructure, Mechanical Properties, and Precipitation Behavior of 1000 MPa Grade GEN3 Steel after Various Quenching Processes

Effect of hot stamping and quenching & partitioning process on microstructure and mechanical properties of ultra-high strength steel

Enhanced Mechanical Properties and Ultrafine Microstructure of 18CrNiMo7-6 Steel Prepared by Quenching and Partitioning Combined Cryogenic Treatment

Effect of Heat Treatment on Microstructure and Properties of Improved 40crni2si2mov Steel

Development of high strength plates with low yield ratio by the combination of TMCP and inter-critical quenching and tempering