Abstract:Long‐time austempering treatment can reduce the volume fraction of brittle martensite. However, the cementite precipitates in the austenite during the long‐time austempering process, which decreases the carbon content in retained austenite (RA) and consequently reduces the mechanical stability of RA. In comparison, excellent mechanical properties were obtained in the samples after short‐time austempering plus tempering treatment. Herein, the microstructure and mechanical properties of a high‐carbon bainitic steel treated by long‐time bainitic austempering and short‐time austempering plus tempering processes are compared. The multiphase microstructures are characterized by dilatometry, X‐ray diffraction, scanning electron microscopy, and transmission electron microscopy to correlate with mechanical properties. Results show that although long‐time austempering treatment can reduce the volume fraction of brittle martensite, no significant improvement is observed in fracture damage resistance. Besides, the cementite is prone to precipitation from the austenite at the later period of the long‐time austempering process. The cementite precipitation in austenite decreases the carbon content in retained austenite (RA) and consequently reduces the mechanical stability of RA. In contrast, the cementite has not been able to precipitate from austenite after short‐time austempering treatment, whereas the martensite is softened and the stability of RA is improved during subsequent tempering. Therefore, excellent mechanical properties are obtained in the samples treated by short‐time austempering plus tempering process: ultimate tensile strength, 1489 MPa, yield strength, 1014 MPa, total elongation, 33.2%, and the product of strength and elongation (PSE) of 48.4 GPa%, where PSE is increased by 27% compared with the sample after long‐time bainitic austempering.

Structure–mechanical Property Relationship in a Low Carbon Nb–Cu Microalloyed Steel Processed Through a Three-Step Heat Treatment: the Effect of Tempering Process

The Influence of Heat Treatment on the Microstructure and Properties of a Cu-Bearing Ultra-Low Carbon Steel

Effects of niobium and heat treatment on microstructure and mechanical properties of low carbon cast steels

Effects of V-Nb microalloying on the microstructure and properties of spring steel under different quenching-tempering times

Effect of Tempering Temperature and Carbide Free Bainite on the Mechanical Characteristics of a High Strength Low Alloy Steel

Effect of Temperature on Microstructure and Mechanical Properties of Fe-9Ni-2Cu Steel during the Tempering Process

Comparison of Microstructure and Mechanical Properties of a High‐Carbon Bainitic Steel Treated by Long‐Time Bainitic Austempering and Short‐Time Austempering Plus Tempering Processes

Microstructure Evolution and Mechanical Properties during Long-term Tempering of a Low Carbon Martensitic Stainless Bearing Steel

Microstructure and Mechanical Properties of Low- and Medium-Carbon Si-Rich Low-Alloy Steels Processed by Austemping after Intercritical Annealing

Microstructural and Mechanical Properties Development During Quenching-Partitioning-Tempering Process of Nb-V-Ti Microalloyed Ultra-High Strength Steel

Effect of Tempering Heat Treatment on the Microstructure and Impact Toughness of a Ni-Cr-Mo-V Steel Weld Metal

Microstructural evolution and mechanical property changes of a new nitrogen-alloyed Cr–Mo–V hot-working die steel during tempering

Crucial Microstructural Features to Determine the Mechanical Properties of Welded Joints in a Cu-Containing Low-Carbon Low-Alloy Steel After Postweld Heat Treatment

Effect of Tempering Temperature on Microstructure and Properties of a New Type of Nitrogen‐Containing Hot‐Work Die Steel 3Cr7Mo2NiSiVN

Effect of Intercritical Annealing Time on Microstructure Evolution and Mechanical Properties of Low Carbon Medium Manganese Steel Subjected to Multi-Step Heat Treatment Process

Effect of Austenitising Temperature on Microstructure and Mechanical Properties of 30si2crni4monb Ultrahigh Strength Steel

Evolution of Microstructures and Mechanical Properties with Tempering Temperature in a Novel Synergistic Precipitation Strengthening Ultra-High Strength Steel

Microstructure and property evolution during tempering of a medium carbon bainitic steel

Variations in microstructure and mechanical properties along thickness direction in a heavy high strength low alloy steel plate

Stability of retained austenite in high carbon steel – Effect of post-tempering heat treatment

The Evolution of a Microstructure during Tempering and Its Influence on the Mechanical Properties of AerMet 100 Steel