Abstract:Abstract PbZr0.52Ti0.48O3 nanocrystals were synthesized by a hydrothermal method. The effect of NaOH concentration, reaction temperature and time on nucleation and growth of PbZr0.52Ti0.48O3 nanocrystals was investigated. As the 0.05 mol/L PbZr0.52Ti0.48O3 precursors were heated at 200 °C for 21 h with NaOH concentration of 0.5 mol/L, the tetragonal PbZr0.52Ti0.48O3 nanocrystals were formed, and the grain size was more than 20 nm. With increasing the NaOH concentration from 0.5 to 1.5 mol/L, the grain size of PbZr0.52Ti0.48O3 nanocrystals decreased. When the precursors were heated at different temperatures (140 °C to 200 °C) for 21 h with 1.0 mol/L NaOH, single-phase PbZr0.52Ti0.48O3 nanocrystals were obtained at 160 °C to 200 °C. With increasing the reaction temperature from 160 °C to 200 °C, the grains size of PbZr0.52Ti0.48O3 nanocrystals increased from 5 nm to 9 nm. When the precursors were heated at 160 °C in different reaction times from 6 h to 21 h, the evolution from amorphous to crystalline PbZr0.52Ti0.48O3 nanocrystals in correlation with the reaction time was observed. Single crystalline PbZr0.52Ti0.48O3 nanocrystals with narrow size distribution (from 5 nm to 9 nm) were synthesized by controlling the NaOH concentration, reaction temperature and time. The obtained results can find potential application in preparing PbZr0.52Ti0.48O3 thin films on flexible substrates.

Preparation and Characterization of Sol–gel Derived ZnTiO3 Nanocrystals

Preparation and Properties of CaTiO_3:Zn Nanoparticles Based on Sol-Gel Method

The Characterization and Preparation of Nano Scale Fe Doping TiO2 by Sol Gel Method? the Crystallization and Thermal Decomposition Process of Fe Doping TiO2 Xerogel Powders Using Thermal TG IR Spectrometry

In-Situ Anatase Flake Crystals Prepared By Sol-Gel Method At Low Temperature

Preparation and Characterization of Na-doped ZnO Thin Films by Sol–gel Method

The Characterization And Preparation Of Nano-Scale Fe Doping Tio2 By Sol-Gel Method - (Ii) - The Crystal Character And Grain Growth Of Fe Doping Tio2 Xerogel Powders

Formation and transformation of ZnTiO3 prepared by sol–gel process

Sol-Gel Preparation of N-doped TiO2 Nanocrystalline at Low Temperature

Preparation of Ti1-xFexO2 Nanocrystals via Low Temperature Sol-Gel Method

Hydrothermal Synthesis and Characterization of Zirconia Nanocrystallites

Synthesis of Single-Crystalline Pb(Zr0.52Ti0.48)O-3 Nanocrystals by Hydrothermal Method

Studies on the nanocrystalline Co3O4 by wet synthesis and its microstructure

Preparation of CuO-TiO2 nanocrystalline powders by the sol-gel method

Preparation And Characterization Of Nano-Yb2o3/Tio2 Particles

Effects of Water Amount and Ph on the Crystal Behavior of a TiO2 Nanocrystalline Derived from a Sol–Gel Process at a Low Temperature

Preparation and characterization of ZnO-B2O3-SO2 by sol-gel method

Silica Zinc Titanate Wide Bandgap Semiconductor Nanocrystallites: Synthesis and Characterization

Synthesis and characterization of nanocrystallite ZnCrFeO4

Preparation and Dielectric Properties of (ca0.61,nd0.26)tio3 Nanoparticles by a Sol–gel Method

Aqueous sol–gel synthesis of zirconium titanate (ZrTiO4) nanoparticles using chloride precursors

Preparation and Characterization of Nanometer TiO_2 Particles in Different Crystal Structures