Abstract:Abstract PbZr0.52Ti0.48O3 nanocrystals were synthesized by a hydrothermal method. The effect of NaOH concentration, reaction temperature and time on nucleation and growth of PbZr0.52Ti0.48O3 nanocrystals was investigated. As the 0.05 mol/L PbZr0.52Ti0.48O3 precursors were heated at 200 °C for 21 h with NaOH concentration of 0.5 mol/L, the tetragonal PbZr0.52Ti0.48O3 nanocrystals were formed, and the grain size was more than 20 nm. With increasing the NaOH concentration from 0.5 to 1.5 mol/L, the grain size of PbZr0.52Ti0.48O3 nanocrystals decreased. When the precursors were heated at different temperatures (140 °C to 200 °C) for 21 h with 1.0 mol/L NaOH, single-phase PbZr0.52Ti0.48O3 nanocrystals were obtained at 160 °C to 200 °C. With increasing the reaction temperature from 160 °C to 200 °C, the grains size of PbZr0.52Ti0.48O3 nanocrystals increased from 5 nm to 9 nm. When the precursors were heated at 160 °C in different reaction times from 6 h to 21 h, the evolution from amorphous to crystalline PbZr0.52Ti0.48O3 nanocrystals in correlation with the reaction time was observed. Single crystalline PbZr0.52Ti0.48O3 nanocrystals with narrow size distribution (from 5 nm to 9 nm) were synthesized by controlling the NaOH concentration, reaction temperature and time. The obtained results can find potential application in preparing PbZr0.52Ti0.48O3 thin films on flexible substrates.

Synthesis of ZnTa2O6 Powder by Molten Salt Method

Molten Salt Synthesis of ZnNb{sub 2}o{sub 6} Powder

Synthesis of ZnO Nano-crystal Powder by Molten Salt Method

Synthesis of MgTa2O6 Nano-Powders by Citrate Sol–gel Method

Synthesis of Pb(Zr0.52Ti0.48)O3(PZT) Powder by A Partial Lead Oxalate Coprecipitation Method

In-situ Synthesis of Nanocrystalline TiC Powders, Nanorods, and Nanosheets in Molten Salt by Disproportionation Reaction of Ti(II) Species

Preparation and Properties of CaTiO_3:Zn Nanoparticles Based on Sol-Gel Method

Molten-salt Synthesis of BaTiO3 Powders and Their Atomic-Scale Structural Characterization

Synthesis of Single-Crystalline Pb(Zr0.52Ti0.48)O-3 Nanocrystals by Hydrothermal Method

Low Temperature Synthesis of ZnNb2O6 Fine Powders by Wet-Chemical Processes

Molten Salt Synthesis of Lead Lanthanum Zirconate Titanate Stannate Powders and Ceramics

Synthesis of Pure Bi<sub>12</sub>SiO<sub>20</sub> Powder by Molten Salt Method

Effect of Raw Material Particle Size on the Synthesis of La 2 Zr 2 O 7 by the Molten Salt Method

Synthesis of ZnTiO3 Ceramic Powders by Sol-Gel Method

Study of the synthetic process of CaBi2Ta2O9 powder by the molten‐salt method

Synthesis of K6ta10.8o30 Nanowires by Molten Salt Technique

Hexavalent Ions Insertion in Garnet Li7 La3 Zr2 O12 Toward a Low Temperature Densification Reaction

Morphological Control of Ba-Ti-O Particles Prepared by Molten Salt Synthesis

Hydrothermally synthesized Pb0.70La0.30TiO3 powders

Low temperature synthesis of (Pb,La)(Zr,Sn,Ti)O 3 powders by citrate process

Hydrothermal synthesis and characterization of (Zr1−xSnx)TiO4 (x = 0.05–0.20) powders