Abstract:The magnesiothermic reduction of SiO 2 is an important reaction as it is a bulk method that produces porous Si for a wide range of applications directly from SiO 2 . While its main advantage is potential tunability, the reaction behavior and final product properties are heavily dependent on many parameters including feedstock type. However, a complete understanding of the reaction pathway has not yet been achieved. Here, using in-situ X-ray diffraction analysis, for the first time, various pathways through which the magnesiothermic reduction reaction proceeds were mapped. Further, the key parameters and conditions that determine which pathways are favored were determined. It was discovered that the reaction onset temperatures can be as low as 348 ± 7°C, which is significantly lower when compared to previously reported values. The onset temperature is dependent on the size of Mg particles used in the reaction. Further, Mg 2 Si was identified as a key intermediate rather than a reaction byproduct during the reduction process. Its rate of consumption is determined by the reaction temperature which needs to be >561°C. These findings can enable process and product optimization of the magnesiothermic reduction process to manufacture and tune porous Si for a range of applications.

Low Temperature Synthesis of Mesoporous Silicon Carbide Via Magnesiothermic Reduction

Low-temperature pseudomorphic transformation of ordered hierarchical macro-mesoporous SiO2/C nanocomposite to SiC via magnesiothermic reduction.

Facile fabrication of three-dimensional mesoporous Si/SiC composites via one-step magnesiothermic reduction at relative low temperature

Preparation of Mesoporous Si Nanoparticles by Magnesiothermic Reduction for the Enhanced Reactivity

Low-temperature formation of nanocrystalline β-SiC with high surface area and mesoporosity via reaction of mesoporous carbon and silicon powder

Synthesis of nanocrystalline silicon carbide powders

Synthesis and formation mechanism of ZrC–SiC–TiC ceramic powders with high-sinterability via sol-gel process and carbothermal reduction

Low Temperature Chemical Reduction of Fusional Sodium Metasilicate Nonahydrate into a Honeycomb Porous Silicon Nanostructure

Synthesis of Silicon Carbide Nanopowder Using Silica Fume

Unlocking the Secrets of Porous Silicon Formation: Insights into Magnesiothermic Reduction Mechanism using In-situ Powder X-ray Diffraction Studies

Template‐Synthesized Porous Silicon Carbide As an Effective Host for Zeolite Catalysts

In Situ Synthesis and Interfacial Bonding Mechanism of SiC in MgO–SiC–C Refractories

High-temperature synthesis of stable ordered mesoporous silica materials using mesoporous carbon as a hard template

Preparation Of Nanocrystalline Silicon Carbide Powders By Carbothermal Reduction

Low temperature synthesis and formation mechanism of dense SiC coating layer by fluidized bed chemical vapor deposition

Mg2Si Promoted Magnesio-Mechanical Reduction of Silica into Silicon Nanoparticles for High-Performance Li-ion Batteries

Mg-catalyzed autoclave synthesis of aligned silicon carbide nanostructures.

Synthesis Nano-Sicp/Mosi2 Composites by In-Situ Reaction Sintering and Low Temperature Oxidation Behavior

Manipulation Of Phase And Microstructure At Nanoscale For Sic In Molten Salt Synthesis

Rapid Synthesis of SiC Powders by Spark Plasma-Assisted Carbothermal Reduction Reaction