Preparation of Nd-doped BaCeO3 proton-conducting ceramic and its electrical properties in different atmospheres

F.L. Chen,O.Toft Sørensen,G.Y. Meng,D.K. Peng

DOI: https://doi.org/10.1016/S0955-2219(97)00136-2

IF: 5.7

1998-01-01

Journal of the European Ceramic Society

Abstract:Nd-doped BaCeO3 was prepared by a conventional ceramic processing technique using a special procedure to reduce calcining and sintering temperatures and to avoid possible contamination. BaCe0.9Nd0.1O3 − α single perovskite phase was formed when the mixture powders was calcined at T ≥1000 °C. Ball-milling of the calcined powders could well disperse agglomerates. Sintered at T ≥ 1300 °C, specimens with density ≥ 93% of the theoretical and without open porosity could be obtained. Electrical conductivity was measured in different dry atmospheres of Ar, air and O2 and in moist air. The results showed that in dry Ar, air and O2, the conductivity values at a given temperature were similar, and the activation energies almost identical, possibly because Nd-doped BaCeO3 demonstrated predominately oxygen ion conduction in these environments. In moist air, proton conduction might predominate, leading to an increase in conductivity and a decrease in activation energy.