Modification of BaTiO3 for Diversified Applications by Single Nd Element Substitution with Wide Doping Range
Fenglin Wang,Haijun Mao,Xingyu Chen,Wei Li,Zhuofeng Liu,Weijun Zhang,Shuxin Bai
DOI: https://doi.org/10.1007/s10854-023-10482-y
2023-01-01
Journal of Materials Science Materials in Electronics
Abstract:In this work, A -site Nd doped BaTiO 3 ceramics in the form of Ba 1− x Nd 2 x /3 TiO 3 with a wide substitution level range of x = 0–0.2 have been prepared via solid-state reaction method. Powder X-ray diffraction results reveal that Nd is completely incorporated into the BaTiO 3 lattice in all specimens. Further analyses based on Rietveld refinement suggest that tetragonal and pseudo-cubic phases coexist in Ba 1− x Nd 2 x /3 TiO 3 ceramics with x ≤ 0.06, and the amount of tetragonal phase is raised with the increase of x value. When x value is larger than 0.08, only pseudo-cubic is observed. The generated V^''_Ba , Nd_Ba^· and V_O^·· defects, which are identified by X-ray photoelectron spectra, make the grain size displays a tendency of decrease first mainly due to the pining effect, and then increase ascribed to the accelerate of mass diffuse. By introducing such wide range of substitution level, Ba 1− x Nd 2 x /3 TiO 3 ceramics with colossal dielectric constant ( x = 0.08), temperature-stable dielectric properties ( x = 0.15), especially relaxor behavior ( x = 0.20) noticed for the first time, are, respectively, received, which is closely related to the variation of phases and defects induced by the addition of Nd. This study may provide a special idea to modify BaTiO 3 to satisfy diversified applications by single element with a wide doping range, and could lay the foundation of future works focusing on the various potential applications of Ba 1− x Nd 2 x /3 TiO 3 ceramics.