Preparation of Nano BaTiO3-based PTC Ceramics Powder and Its Electrical Properties

DING Shi-wen,JIA Guang,AN Cai-xiu

DOI: https://doi.org/10.3969/j.issn.1007-4252.2007.04.015

2007-01-01

Abstract:The H2TiO3 through hydrolysis of TiCl4 and calculated amount of Ba(OH)2·8H2O Sr(Ac)2·1/2H2O,Mn(Ac)2·4H2O and Y(Ac)3 were mixed and ground in mortar for 1h at room temperature,then dried at 100℃.The Ba0.85-xYx Sr0.07Ca0.08 MnyTi1yO3 powder was obtained by calcining the mixture at 800℃ for 1h.XRD pattern demonstrated that the compounds were mutually miscible in the solid solutions.The TEM photograph showed that the compounds had a shape of uniform,substantially spherical particles with an average partical size of 50 nm in diameter.The PTC effect of the materials were studied by using prepared ceramics.It was found that the resistance is near 13Ω at room temperature,ratio of lg(Rmax/Rmin)is 6 and temperature coefficient of resistance α is 21.9% / ℃ when the content of Y and Mn are 1 mol% and 0.04 mol% respectively.