Abstract:The potential of calcium-doped layered perovskite compounds, BaNd1–xCaxInO4–x/2 (where x is the excess Ca content), as protonic conductors was experimentally investigated. The acceptor-doped ceramics exhibit improved total conductivities that were 1–2 orders of magnitude higher than those of the pristine material, BaNdInO4. The highest total conductivity of 2.6 × 10–3 S cm–1 was obtained in the BaNd0.8Ca0.2InO3.90 sample at a temperature of 750 °C in air. Electrochemical impedance spectroscopy measurements of the x = 0.1 and x = 0.2 substituted samples showed higher total conductivity under humid environments than those measured in a dry environment over a large temperature range (250–750 °C). At 500 °C, the total conductivity of the 20% substituted sample in humid air (∼3% H2O) was 1.3 × 10–4 S cm–1. The incorporation of water vapor decreased the activation energies of the bulk conductivity of the BaNd0.8Ca0.2InO3.90 sample from 0.755(2) to 0.678(2) eV in air. The saturated BaNd0.8Ca0.2InO3.90 sample contained 2.2 mol % protonic defects, which caused an expansion in the lattice according to the high-temperature X-ray diffraction data. Combining the studies of the impedance behavior with four-probe DC conductivity measurements obtained in humid air, which showed a decrease in the resistance of the x = 0.2 sample, we conclude that experimental evidence indicates that BaNd1–xCaxInO4–x/2 is a fast proton conductor.This article has not yet been cited by other publications.

Protonic Conduction in the BaNdInO 4 Structure Achieved by Acceptor Doping

Optimising Ion Conductivity in NdBaInO4-Based Phases

(La1-x Mx )2 (Nb0.45 Yb0.55 )2 O7-δ (M=Ca, Sr, Ba) Ionic Conductors Promoted by Foreign/Domestic Dual Acceptor-Doping Strategies

High proton conduction by full hydration in highly oxygen deficient perovskite

Simultaneous Hetero- and Isovalent Doping as the Strategy for Improving Transport Properties of Proton Conductors Based on BaLaInO4

Novel Chemically Stable Ba3Ca1.18Nb1.82-xYxO9-delta Proton Conductor: Improved Proton Conductivity through Tailored Cation Ordering

High proton conductivity within the ‘Norby gap’ by stabilizing a perovskite with disordered intrinsic oxygen vacancies

Synthesis, Structure and Protonic Conduction of Basn0.875m0.125o3-Delta (M = Sc, Y, in and Gd)

Samarium and Yttrium Codoped BaCeO3 Proton Conductor with Improved Sinterability and Higher Electrical Conductivity

2D Doping of Proton Conductors: BaZrO 3 ‐Based Heterostructures

Use of Interplay between A‐Site Non‐Stoichiometry and Hydroxide Doping to Deliver Novel Proton‐Conducting Perovskite Oxides

Transport Properties of Highly Dense Proton-Conducting BaSn 1 _ X in X O 3 _ Δ Ceramics

Transport Properties of Highly Dense Proton-Conducting BaSn1−xInxO3−δ Ceramics

Mixed Conduction in A-Site Double-Perovskite Na1+xLa1-xZr2O6-δ Proton Conductors

Doping Effects In (Ba0.85ca0.15)(Hf0.1ti0.9)O-3 Lead-Free Piezoelectric Ceramics Prepared Via Powder Injection Moulding Using Simple Binder

Proton Transport in the Gadolinium-Doped Layered Perovskite BaLaInO4

Anisotropic Proton and Oxygen Ion Conductivity in Epitaxial Ba2In2O5 Thin Films

Influence of ZnO Additive on the Properties of Y-doped BaSnO3 Proton Conductor

Preparation of Nd-doped BaCeO3 proton-conducting ceramic and its electrical properties in different atmospheres

Pressure-induced negative capacitance and enhanced grain boundary conductivity in nanocrystalline solid electrolyte BaZrO 3

High Proton Conduction in the Octahedral Layers of Fully Hydrated Hexagonal Perovskite-Related Oxides