Abstract:Chemical vapor infiltration of carbon fiber felts with uniform initial bulk density of 0.47 g·cm −3 was investigated at the ethanol partial pressures of 5–20 kPa, as well as the temperatures of 1050, 1100, 1150 and 1200°C. Ethanol, diluted by nitrogen, was employed as the precursor of pyrolytic carbon. Polarized light microscopy (PLM), scanning electron microscopy and X-ray diffraction were adopted to study the texture of pyrolytic carbon deposited at various temperatures. A change from medium- to high-textured pyrolytic carbon was observed in the sample infiltrated at 1050°C. Whereas, homogeneous high-textured pyrolytic carbons were deposited at the temperatures of 1100, 1150 and 1200°C. Extinction angles of 19°–21° were determined for different regions in the samples densified at the temperatures ranging from 1100 to 1200°C. Scanning electron microscopy of the fracture surface after bending test indicated that the prepared carbon/carbon composite samples exhibited a pseudo-plastic fracture behavior. In addition, fracture behavior of the carbon/carbon samples was obviously effected by their infiltration temperature. The fracture mode of C/C composites was transformed from shearing failure to tensile breakage with increasing infiltration temperature. Results of this study show that ethanol is a promising carbon source to synthesize carbon/carbon composites with homogeneously high-textured pyrolytic carbon over a wide range of temperatures (from 1100 to 1200°C).

Densification Mechanism of Chemical Vapor Infiltration Technology for Carbon/carbon Composites

Research on chemical vapor infiltration of pyrolytic carbon for carbon/carbon composites

The Influence of Hydrocarbon Gas on the Density and Microstructure of C/C Composites Formed by Chemical Vapor Infiltration

Effect of Oxygen and Hydrogen on Microstructure of Pyrolytic Carbon Deposited from Thermal Decomposition of Methane and Ethanol

Rapid Densification of Carbon/Carbon Composites Plate by Pressure‐Gradient Chemical Vapor Infiltration

Research Situation of Densification Technologies for Carbon/carbon Composites

Kinetics of Chemical Vapor Infiltration of Carbon Nanofiber-Reinforced Carbon/Carbon Composites

Research on Parameter of Preparation of Pyrocarbon with Chemical Vapor Infiltration

Densification of unidirectional carbon–carbon composites by isothermal chemical vapor infiltration

Study on chemical liquid-vaporized infiltration process for preparing carbon/carbon composites

Microstructure Of Pyrocarbon With Chemical Vapor Infiltration

Preparation and Properties of Density Gradient Carbon/Carbon Composites

Carbon/carbon composites preparation by novel technology and its characteristic

Carbon infiltration of carbon-fiber preforms by catalytic CVI

Influence of Infiltration Pressure on the Densification Rate and Microstructure of Pyrocarbon During Chemical Vapor Infiltration

Influence of the Factors of CVI Technology on Densification of C/C Composites

Progress in Research on Chemicai Liquid-Vaporized Infiltration for C/C Composites

Densification and Microstructure of Carbon/carbon Composites Prepared by Chemical Vapor Infiltration Using Ethanol As Precursor

Study on Microstructure and Mechanical Properties of Carbon/Carbon Composite Obtained by Chemical Vapor Infiltration

Densification Behavior and Microstructure of Carbon/carbon Composites Prepared by Chemical Vapor Infiltration from Xylene at Temperatures Between 900 and 1250 °C

Effect of chemical vapor infiltration on the flexural properties of C/C-SiC composites prepared by the precursor infiltration pyrolysis method