Abstract:Low-density xSiO2-(1-x)Al2O3 xerogels with x=0.9,0.8,0.7 and 0.6(mole fractions) were prepared by sol-gel and non-supercritical drying.Silica alkogels,which were the network supports of binary composite materials,formed from TEOS by hydrolytic condensation with a molar ratio of TEOS∶H2O∶ alcohol∶ HCl∶ammonia=1∶4∶10∶7.5×10-4∶0.0375.Aluminum hydroxide derived from Al(NO3)3 and NH4OH acting in the alcohol solution under the condition of catalysts.The structural changes and crystallization of the binary xerogels were investigated after heating at 300,600,900,1200℃ for 2h by the means of nitrogen adsorption experiments,X-ray diffraction,FT-IR spectroscopy,SEM and TEM.The resulting mixed xerogels possess of nano-mesoporous structure which is characteristic of the amorphous framework and crystal Al2O3,high specific surface area and a relatively narrow pore distribution.Al2O3 introduces into the SiO2 phase and some of Si-O-Al bonds form,the amount of which increases with the aluminum content increasing.The alumina-containing xerogles before calcinations are well-crystallized γ-AlOOH that converts to γ-alumina or α-alumina by calcination.The binary xerogels improve the thermal resistance in comparison with the pure SiO2 xerogels because of the presence of Al2O3 in the network.

Porous Structure Characteristic of the Additive Silica Xerogels by SAXS

SAXS investigations of the fractal character of additive silica xerogels

Fractal Characteristic of Silica Xerogels with Different Additives

Fractal characteristic of additive silica xerogels by SAXS

Effect of the adulterants on pore structure of silica xerogels

Preparation and Structure Analysis of Silica Xerogels

Synthesis and structural characterization of SiO2-Al 2O3 xerogels

POROUS STRUCTURE CHARACTERISTICS OF SiO2-Al2O3 XEROGELS BY NITROGEN ADSORPTION-DESORPTION METHOD

Microstructure and Mechanical Properties of Silica Xerogels Doped with Sic Whisker and Short Carbon Fiber

Effect of Heat Treatment on Texture and Structure of Silica Xerogels

Effect of SiO_2 Addition on the Properties of Fe_2O_3-SiO_2 Binary Composite Xerogels

Synthesis and Structural Characterization of SiO<sub>2</sub>-Al<sub>2</sub>O<sub>3</sub> Xerogels

Pore Structures of Methyl-Modified Silica Xerogels by Small Angle X-Ray Scattering

Study on the Structure of Fe2O3 Xerogels by Small Angle X-ray Scattering

Evolution of pore and surface characteristics of silica xerogels during calcining

Influence of Additives on Pore Size Distributions of Silica Aergels

Application of Drying Control Chemical Additives in Preparation for Silica Aerogels

The Orthogonal Optimization of Process Parameters of Silica Xerogels

Influence of Drying Procedure on the Mesoporosity and Surface Fractal Dimensions of Silica Xerogels Prepared with Different Agitation Methods

The Synthesis and Characterization of SiO_2-Al_2O_3 Xerogels